SABIC Innovative Plastics Lexan® 3441R PC (Europe-Africa-Middle East)

Category	Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer	SABIC Innovative Plastics (GE Plastics)
Trade Name	Lexan®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	SABIC Innovative Plastics Lexan® 3441R PC (Europe-Africa-Middle East).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Lexan 3441R is a medium viscosity, 10% glass reinforced polycarbonate grade, compliant with European food contact regulation EC Directive 2002/72/EC. The grade is especially designed for applications requiring high rigidity and higher heat resistance.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.

Physical Properties	Metric	English	Comments
Density	1.25 g/cc	0.0452 lb/in³	ISO 1183
Moisture Absorption at Equilibrium	0.13 %	0.13 %	23°C / 50% RH; ISO 62
Water Absorption at Saturation	0.31 % @Temperature 23.0 °C	0.31 % @Temperature 73.4 °F	ISO 62
Linear Mold Shrinkage, Flow	0.0020 - 0.0060 cm/cm	0.0020 - 0.0060 in/in	on tensile bar; SABIC Method
Melt Flow	8.0 g/10 min @Load 1.20 kg, Temperature 300 °C	8.0 g/10 min @Load 2.65 lb, Temperature 572 °F	[cm^3/10 min] Melt Volume Rate; ISO 1133

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	45.0 MPa	6530 psi	5 mm/min; ISO 527
Tensile Strength, Yield	60.0 MPa	8700 psi	5 mm/min; ISO 527
Elongation at Break	7.0 %	7.0 %	5 mm/min; ISO 527
Elongation at Yield	5.0 %	5.0 %	5 mm/min; ISO 527
Tensile Modulus	3.30 GPa	479 ksi	1 mm/min; ISO 527
Flexural Yield Strength	95.0 MPa	13800 psi	2 mm/min; ISO 178
Flexural Modulus	3.40 GPa	493 ksi	2 mm/min; ISO 178
Izod Impact, Notched (ISO)	8.00 kJ/m² @Temperature -30.0 °C	3.81 ft-lb/in² @Temperature -22.0 °F	80103; ISO 180/1A
	10.0 kJ/m² @Temperature 23.0 °C	4.76 ft-lb/in² @Temperature 73.4 °F	80103; ISO 180/1A
Izod Impact, Unnotched (ISO)	130 kJ/m² @Temperature -30.0 °C	61.9 ft-lb/in² @Temperature -22.0 °F	80103; ISO 180/1U
	NB @Temperature 23.0 °C	NB @Temperature 73.4 °F	80103; ISO 180/1U
Charpy Impact Unnotched	NB @Temperature 23.0 °C	NB @Temperature 73.4 °F	Edgew 80103 sp=62mm; ISO 179/1eU
	NB @Temperature -30.0 °C	NB @Temperature -22.0 °F	Edgew 80103 sp=62mm; ISO 179/1eU
Charpy Impact, Notched	0.900 J/cm² @Temperature -30.0 °C	4.28 ft-lb/in² @Temperature -22.0 °F	V-notch Edgew 80103 sp=62mm; ISO 179/1eA
	1.00 J/cm² @Temperature 23.0 °C	4.76 ft-lb/in² @Temperature 73.4 °F	V-notch Edgew 80103 sp=62mm; ISO 179/1eA

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	40.0 µm/m-°C @Temperature -40.0 - 40.0 °C	22.2 µin/in-°F @Temperature -40.0 - 104 °F	ISO 11359-2
CTE, linear, Transverse to Flow	40.0 µm/m-°C @Temperature -40.0 - 40.0 °C	22.2 µin/in-°F @Temperature -40.0 - 104 °F	ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi)	140 °C	284 °F	Edgew 120104 sp=100mm; ISO 75/Be
Deflection Temperature at 1.8 MPa (264 psi)	132 °C	270 °F	Edgew 120104 sp=100mm; ISO 75/Ae
	136 °C @Treatment Temp. 120 °C, Time 7200 sec	277 °F @Treatment Temp. 248 °F, Time 2.00 hour	annealed; ISO 75/Ae
Vicat Softening Point	141 °C	286 °F	Rate B/50; ISO 306
	143 °C	289 °F	Rate B/120; ISO 306
Glow Wire Test	850 °C @Thickness 1.60 mm	1560 °F @Thickness 0.0630 in	Glow Wire Flammability Index; IEC 60695-2-12