NOVA Chemicals Sclair® 11G1 LLDPE Film Resin  (discontinued **)

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE), Film Grade
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF NOVA Chemicals Sclair® 11G1 LLDPE Film Resin  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Low gel, Excellent seal characteristics, Easy processabilityApplications: Premium shrink film, Co-extrusionAdditives: Process stabilizer, Polymer process aidFilm properties are typical of blown film extruded at a blowup ratio of 2.5:1, but are dependent upon operating conditions.Information provided by NOVA Chemicals.
Physical Properties Metric English Comments
Density 0.920 g/cc
0.0332 lb/in³
ASTM D792
Thickness 25.0 - 75.0 microns
0.984 - 2.95 mil
Melt Flow 0.72 g/10 min

@Load 2.16 kg,
Temperature 190 °C
0.72 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 10.0 MPa
1450 psi
ASTM D882
Film Tensile Strength at Yield, TD 11.0 MPa
1600 psi
ASTM D882
Film Elongation at Break, MD 620 %
620 %
ASTM D882
Film Elongation at Break, TD 920 %
920 %
ASTM D882
Secant Modulus, MD 0.180 GPa
26.1 ksi
at 1%; ASTM D882
Secant Modulus, TD 0.200 GPa
29.0 ksi
at 1%; ASTM D882
Coefficient of Friction >= 1.0
>= 1.0
ASTM D1894
Elmendorf Tear Strength, MD 18.0 g/micron
457 g/mil
ASTM D1922
Elmendorf Tear Strength, TD 26.0 g/micron
660 g/mil
ASTM D1922
Dart Drop 8.00 g/micron
203 g/mil
F<sub>50</sub>, ASTM D1709/A
Film Tensile Strength at Break, MD 43.0 MPa
6240 psi
ASTM D882
Film Tensile Strength at Break, TD 36.0 MPa
5220 psi
ASTM D882
Optical Properties Metric English Comments
Haze 11 %
11 %
1 mil; ASTM D1003
Gloss 51 %
51 %
at 45°; 1 mil; ASTM D2457
Processing Properties Metric English Comments
Melt Temperature 220 - 230 °C
428 - 446 °F
Die Opening 0.0900 - 0.220 cm
0.0354 - 0.0866 in
Descriptive Properties Value Comments
Blow Up Ratio 2:1 to 3:1