SABIC Innovative Plastics LNP THERMOTUF VF008 Super Tough Nylon
| Category | Polymer , Thermoplastic , Nylon |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP Thermotuf |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOTUF VF008 Super Tough Nylon.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP THERMOTUF* VF008 is a compound based on Super Tough Nylon resin containing Glass Fiber. Added features of this material include: High Impact.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.38 g/cc | 1.38 g/cc | ASTM D792 |
| Density | 1.40 g/cc | 0.0506 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.450 % | 0.450 % | 50% RH, 24 hrs; ASTM D570 |
| 0.660 % | 0.660 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Time 86400 sec |
0.0050 - 0.0070 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.030 cm/cm @Time 86400 sec |
0.010 - 0.030 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 126 MPa | 18300 psi | Type I, 5 mm/min; ASTM D638 |
| 127 MPa | 18400 psi | 5 mm/min; ISO 527 | |
| 131 MPa | 19000 psi | ASTM D638 | |
| Elongation at Break | 3.0 % | 3.0 % | ASTM D638 |
| 3.3 % | 3.3 % | Type I, 5 mm/min; ASTM D638 | |
| 3.3 % | 3.3 % | 5 mm/min; ISO 527 | |
| Elongation at Yield | 3.2 % | 3.2 % | Type I, 5 mm/min; ASTM D638 |
| 3.2 % | 3.2 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 9.90 GPa | 1440 ksi | 1 mm/min; ISO 527 |
| 10.28 GPa | 1491 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 193 MPa | 28000 psi | ASTM D790 |
| 194 MPa | 28100 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| 201 MPa | 29200 psi | ISO 178 | |
| Flexural Yield Strength | 199 MPa | 28900 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 8.53 GPa | 1240 ksi | 2 mm/min; ISO 178 |
| 8.60 GPa | 1250 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| 9.64 GPa | 1400 ksi | ASTM D790 | |
| Izod Impact, Notched | 1.71 J/cm | 3.20 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 10.5 J/cm | 19.7 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 17.0 kJ/m² | 8.09 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 58.0 kJ/m² | 27.6 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 9.00 J @Temperature 23.0 °C |
6.64 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 5.00 J | 3.69 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 32.4 µm/m-°C @Temperature -40.0 - 40.0 °C |
18.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| Thermal Conductivity | 0.380 W/m-K | 2.64 BTU-in/hr-ft²-°F | ASTM E 1530 |
| Deflection Temperature at 0.46 MPa (66 psi) | 255 °C | 491 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 258 °C @Thickness 3.20 mm |
496 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 238 °C | 460 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 245 °C @Thickness 3.20 mm |
473 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Polycasa Lumina CAST PMMA
- Parker Chomerics Tecknit Teckfilm™ Transparent Conductive Coating on Polyester Film
- Plaslok 308 Black (COM) Mineral/Flock Filled Phenolic Molding Compound (discontinued **)
- Supreme Petrochem SC 206 General Purpose Polystyrene
- ExxonMobil 100 Mobiltemp SHC Series
- DuPont Performance Polymers Crastin® SK642FR NC010 Polybutylene Terephthalate (PBT)
- Epoxy Technology EPO-TEK® 320NC-2 Optically Opaque Epoxy
- 3M 2542/Silver Damping Foils
- Bhansali Engineering Abstron IM-16M ABS Very High Rigidity Injection Molding Grade
Copyright © lookpolymers.com All Rights Reserved