LATI Lapex A G/10 PES, 10% Glass Fiber Reinforced

Category Polymer , Thermoplastic , Polyethersulfone (PES) , Polyethersulfone (PES), 10%Glass Fiber Filled
Manufacturer LATI
Trade Name Lapex
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Lapex A G/10 PES, 10% Glass Fiber Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Polyether Sulfone (PES) based compound. Glass fibers. Low smoke density and low toxicity index. Very high dimensional stability.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.45 g/cc
0.0524 lb/in³
Linear Mold Shrinkage, Flow 0.0040 - 0.0055 cm/cm
0.0040 - 0.0055 in/in
Linear Mold Shrinkage, Transverse 0.0080 - 0.0095 cm/cm
0.0080 - 0.0095 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 70.0 MPa

@Temperature 150 °C
 10200 psi

@Temperature 302 °F
75.0 MPa

@Temperature 120 °C
 10900 psi

@Temperature 248 °F
90.0 MPa

@Temperature 90.0 °C
 13100 psi

@Temperature 194 °F
95.0 MPa

@Temperature 60.0 °C
 13800 psi

@Temperature 140 °F
100 MPa

@Temperature 23.0 °C
 14500 psi

@Temperature 73.4 °F
Elongation at Break 3.5 %

@Temperature 23.0 °C
 3.5 %

@Temperature 73.4 °F
3.7 %

@Temperature 60.0 °C
 3.7 %

@Temperature 140 °F
4.1 %

@Temperature 90.0 °C
 4.1 %

@Temperature 194 °F
4.4 %

@Temperature 120 °C
 4.4 %

@Temperature 248 °F
20 %

@Temperature 150 °C
 20 %

@Temperature 302 °F
Elongation at Yield 3.2 %

@Temperature 150 °C
 3.2 %

@Temperature 302 °F
Tensile Modulus 4.10 GPa

@Temperature 150 °C
 595 ksi

@Temperature 302 °F
4.30 GPa

@Temperature 120 °C
 624 ksi

@Temperature 248 °F
4.40 GPa

@Temperature 90.0 °C
 638 ksi

@Temperature 194 °F
4.50 GPa

@Temperature 60.0 °C
 653 ksi

@Temperature 140 °F
4.60 GPa

@Temperature 23.0 °C
 667 ksi

@Temperature 73.4 °F
Charpy Impact Unnotched 5.00 J/cm²
23.8 ft-lb/in²
Charpy Impact, Notched 0.350 J/cm²
1.67 ft-lb/in²
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 180 °C
356 °F
Deflection Temperature at 0.46 MPa (66 psi) 220 °C
428 °F
Deflection Temperature at 1.8 MPa (264 psi) 215 °C
419 °F
Vicat Softening Point 220 °C

@Load 5.00 kg
 428 °F

@Load 11.0 lb
Flammability, UL94 V-0

@Thickness 3.00 mm
 V-0

@Thickness 0.118 in
V-0

@Thickness 1.50 mm
 V-0

@Thickness 0.0591 in
Oxygen Index 39 %
39 %
Processing Properties Metric English Comments
Melt Temperature 350 - 370 °C
662 - 698 °F
Mold Temperature 140 - 165 °C
284 - 329 °F
Drying Temperature 150 - 180 °C

@Time 10800 sec
 302 - 356 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa