SABIC Innovative Plastics LNP THERMOTUF PF006I PA 6
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP Thermotuf |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOTUF PF006I PA 6.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP THERMOTUF* PF006I is a compound based on Nylon 6 resin containing Glass Fiber. Added features of this material include: High Impact.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.35 g/cc | 1.35 g/cc | ASTM D792 |
| Density | 1.35 g/cc | 0.0488 lb/in³ | ASTM D792 |
| 1.37 g/cc | 0.0495 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.830 % | 0.830 % | 23°C / 50% RH; ISO 62 |
| 0.830 % | 0.830 % | 50% RH, 24 hrs; ASTM D570 | |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0030 cm/cm @Time 86400 sec |
0.0010 - 0.0030 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0011 - 0.0030 cm/cm @Time 86400 sec |
0.0011 - 0.0030 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0062 - 0.0067 cm/cm @Time 86400 sec |
0.0062 - 0.0067 in/in @Time 24.0 hour |
ISO 294 |
| 0.0090 - 0.020 cm/cm @Time 86400 sec |
0.0090 - 0.020 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 97.0 MPa | 14100 psi | Type I, 5 mm/min; ASTM D638 |
| 99.0 MPa | 14400 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 35.0 MPa | 5080 psi | 5 mm/min; ISO 527 |
| 50.0 MPa | 7250 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 8.1 % | 8.1 % | Type I, 5 mm/min; ASTM D638 |
| Tensile Modulus | 9.65 GPa | 1400 ksi | 1 mm/min; ISO 527 |
| 16.23 GPa | 2354 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 157 MPa | 22800 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 6.82 GPa | 989 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Izod Impact, Notched | 1.06 J/cm | 1.99 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 7.27 J/cm | 13.6 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 10.0 kJ/m² | 4.76 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 53.0 kJ/m² | 25.2 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 16.0 J | 11.8 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 4.00 J | 2.95 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 141 °C | 286 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 139 °C @Thickness 3.20 mm |
282 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 135 °C | 275 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 137 °C @Thickness 3.20 mm |
279 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
UL 94 by SABIC-IP |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Cycoloy® RCY6214 PC+ABS (Asia Pacific)
- PolyOne Geon™ 170 Series 4195 Polyvinyl Chloride Homopolymer (PVC Homopolymer)
- Kraton® G1650 + PPE blend (10/90)
- Shinil Chemical SHINNANO PA-66 Polymer Nanocomposite Window Strip
- A. Schulman INVISION™ VX-5170UE Soft Touch Polyolefin Thermoplastic
- Unitika elitel UE3216 Polyester, Pellet
- DSM Novamid® 1010G30 NA PA6-GF30
- Braskem TR3020C Random Copolymer Polypropylene
- Advanced Polymer Alloys DuraGrip™ 6830 Thermoplastic Elastomer
Copyright © lookpolymers.com All Rights Reserved