Hexcel® HexWeb® HRH-10 - 1/4 - 2.0 Aramid Fiber/Phenolic Resin Honeycomb

Category Other Engineering Material , Composite Core Material , Composite Fibers , Polymer , Thermoset , Aramid , Phenolic
Manufacturer Hexcel
Trade Name HexWeb®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Hexcel® HexWeb® HRH-10 - 1/4 - 2.0 Aramid Fiber/Phenolic Resin Honeycomb.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Designation: Material-Cell Size-Density.Hexweb HRH-10 is manufactured from NOMEX aramid fiber sheets. A thermosetting adhesive is used to bond these sheets at the nodes, and after expanding to the hexagonal or OX-Core confiation, the block is dipped in phenolic resin. After curing the resin, slices are cut to the desired thickness. For special applications, such as air directionalizing, HexWeb HRH-10 can be provided without the phenolic resin. Using this process, a wide range of cell sizes, paper thicknesses, and densities can be produced.Information provided by HexCel
Physical Properties Metric English Comments
Density 0.0320 g/cc
0.00116 lb/in³
Mechanical Properties Metric English Comments
Compressive Yield Strength >= 0.793 MPa
>= 115 psi
Bare, min
>= 0.862 MPa
>= 125 psi
Stabilized, min
0.965 MPa
140 psi
Bare, typ
1.07 MPa
155 psi
Stabilized, typ
Compressive Modulus 0.0758 GPa
11.0 ksi
Stabilized, typ
Shear Modulus 0.0138 GPa
2.00 ksi
Plate Shear, W Direction, typ
0.0276 GPa
4.00 ksi
Plate Shear, L Direction, typ
Shear Strength >= 0.276 MPa
>= 40.0 psi
Plate Shear, W Direction, min
0.345 MPa
50.0 psi
Plate Shear, W Direction, typ
>= 0.586 MPa
>= 85.0 psi
Plate Shear, L Direction, min
0.724 MPa
105 psi
Plate Shear, L Direction, typ