SABIC Innovative Plastics LNP THERMOCOMP RFB44XE PA 66 (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP RFB44XE PA 66 (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Thermocomp* RFB44XE is a compound based on Nylon 66 resin containing Glass Fiber, Glass Bead. Added features of this material include: Easy Molding.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.45 g/cc | 0.0524 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0060 cm/cm | 0.0040 - 0.0060 in/in | on Tensile Bar; SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 143 MPa | 20700 psi | 5 mm/min; ISO 527 |
| Tensile Strength, Yield | 29.0 MPa | 4210 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 2.9 % | 2.9 % | 5 mm/min; ISO 527 |
| Elongation at Yield | 0.60 % | 0.60 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 8.60 GPa | 1250 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 203 MPa | 29400 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 6.80 GPa | 986 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² | 2.86 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 40.0 kJ/m² | 19.0 ft-lb/in² | 80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 33.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
18.3 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 80.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
44.4 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 250 °C | 482 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 226 °C | 439 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
Users viewing this material also viewed the following:
- LNP Stat-Kon® LC-1003 Polyetheretherketone, Carbon Fiber Reinforcement (discontinued **)
- Polycasa Acryl® KR 2010/1 Acrylic, Impact Grade
- Lubrizol Advanced Materials Pearlstick® 49-46/03 Linear Thermoplastic Polyurethane Elastomer (discontinued **
- Haysite HCR-197 Corrosion Resistant Polyester/Glass Sheet
- Ineos ABS Lustran® ABS M406
- Techmer ES HiFill FR® PA6/6 GB30 FR 30% Glass Bead Filled
- Techmer ES HiFill® PBT GF30 30% Glass Filled
- A. Schulman POLYFORT™ FPP 3459 Glass Filled Impact Copolymer
- Hexcel® HexWeb® CFC™-20-1/8-11.0 Composite Flooring Honeycomb Core
- Solvay RHODASURF® BC-720 Surfactant
Copyright © lookpolymers.com All Rights Reserved