SABIC Innovative Plastics LNP THERMOCOMP PH0460A PA 6
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP PH0460A PA 6.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOCOMP* PH0460A is a compound based on Nylon 6. Added feature of this material is: High Specific Gravity.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 4.49 g/cc | 0.162 lb/in³ | ISO 1183 |
| 4.51 g/cc | 0.163 lb/in³ | ASTM D792 | |
| Moisture Absorption | 0.100 % | 0.100 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.011 - 0.013 cm/cm @Time 86400 sec |
0.011 - 0.013 in/in @Time 24.0 hour |
ASTM D955 |
| 0.012 cm/cm @Time 86400 sec |
0.012 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.011 - 0.013 cm/cm @Time 86400 sec |
0.011 - 0.013 in/in @Time 24.0 hour |
ASTM D955 |
| 0.012 cm/cm @Time 86400 sec |
0.012 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 56.0 MPa | 8120 psi | ASTM D638 |
| 56.0 MPa | 8120 psi | ISO 527 | |
| Tensile Strength, Yield | 55.0 MPa | 7980 psi | ISO 527 |
| 59.0 MPa | 8560 psi | ASTM D638 | |
| Elongation at Break | 0.80 % | 0.80 % | ISO 527 |
| 1.0 % | 1.0 % | ASTM D638 | |
| Elongation at Yield | 0.80 % | 0.80 % | ISO 527 |
| 0.90 % | 0.90 % | ASTM D638 | |
| Tensile Modulus | 8.43 GPa | 1220 ksi | 1 mm/min; ISO 527 |
| 9.65 GPa | 1400 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 93.0 MPa | 13500 psi | ISO 178 |
| 96.0 MPa | 13900 psi | ASTM D790 | |
| Flexural Modulus | 7.80 GPa | 1130 ksi | ISO 178 |
| 8.27 GPa | 1200 ksi | ASTM D790 | |
| Izod Impact, Notched | 0.420 J/cm | 0.787 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 1.44 J/cm | 2.70 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² | 1.90 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 16.0 kJ/m² | 7.61 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 7.00 J | 5.16 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 2.00 J | 1.48 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 42.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
23.3 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 43.2 µm/m-°C @Temperature -40.0 - 40.0 °C |
24.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| CTE, linear, Transverse to Flow | 45.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
25.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 45.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
25.0 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 196 °C | 385 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 196 °C @Thickness 3.20 mm |
385 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 149 °C | 300 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 156 °C @Thickness 3.20 mm |
313 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Kolon KOCETAL® LF302 Wear Modified Acetal Resin
- Teknor Apex Monprene® MP 1093L Thermoplastic Elastomer
- Unifrax Fiberfrax® Topcoat™ M Coating Cement
- Wall Colmonoy COLMONOY® 88 Hard-Surfacing Alloy
- Covestro Desmopan® DP 3059D Polyurethane
- ExxonMobil LDPE LD 363BR Low Density Polyethylene Resin
- CMW® ELKONIUM 40 pure palladium
- California Fine Wire Nickel Alloy 180 Copper Nickel Resistance Wire
- DuPont Performance Polymers Zytel® HTN FR52G30BL BK337 Polyphthalamide (PPA) (Unverified Data**)
Copyright © lookpolymers.com All Rights Reserved