SABIC Innovative Plastics LNP THERMOCOMP PH0460A PA 6 (Asia Pacific)

Category Polymer , Thermoplastic , Nylon , Nylon 6
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP THERMOCOMP
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP THERMOCOMP PH0460A PA 6 (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* Thermocomp* PH0460A is a compound based on Nylon 6 resin containing High Specific Gravity Filler. Added features of this material include: High Specific Gravity.
Physical Properties Metric English Comments
Density 4.49 g/cc
0.162 lb/in³
ISO 1183
4.51 g/cc
0.163 lb/in³
ASTM D792
Moisture Absorption 0.100 %
0.100 %
50% RH, 24 hrs; ASTM D570
Linear Mold Shrinkage, Flow 0.011 - 0.013 cm/cm

@Time 86400 sec
0.011 - 0.013 in/in

@Time 24.0 hour
ASTM D955
0.012 cm/cm

@Time 86400 sec
0.012 in/in

@Time 24.0 hour
ISO 294
Linear Mold Shrinkage, Transverse 0.011 - 0.013 cm/cm

@Time 86400 sec
0.011 - 0.013 in/in

@Time 24.0 hour
ASTM D955
0.012 cm/cm

@Time 86400 sec
0.012 in/in

@Time 24.0 hour
ISO 294
Mechanical Properties Metric English Comments
Tensile Strength at Break 56.0 MPa
8120 psi
ASTM D638
56.0 MPa
8120 psi
ISO 527
Tensile Strength, Yield 55.0 MPa
7980 psi
ISO 527
59.0 MPa
8560 psi
ASTM D638
Elongation at Break 0.80 %
0.80 %
ISO 527
1.0 %
1.0 %
ASTM D638
Elongation at Yield 0.80 %
0.80 %
ISO 527
0.90 %
0.90 %
ASTM D638
Tensile Modulus 8.43 GPa
1220 ksi
1 mm/min; ISO 527
9.65 GPa
1400 ksi
50 mm/min; ASTM D638
Flexural Strength 93.0 MPa
13500 psi
ISO 178
96.0 MPa
13900 psi
ASTM D790
Flexural Modulus 7.80 GPa
1130 ksi
ISO 178
8.27 GPa
1200 ksi
ASTM D790
Izod Impact, Notched 0.420 J/cm
0.787 ft-lb/in
ASTM D256
Izod Impact, Unnotched 1.44 J/cm
2.70 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 4.00 kJ/m²
1.90 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 16.0 kJ/m²
7.61 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 7.00 J
5.16 ft-lb
Instrumented Impact Energy @ peak; ASTM D3763
Impact Test 2.00 J
1.48 ft-lb
Multiaxial Impact; ISO 6603
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 42.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
23.3 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
43.2 µm/m-°C

@Temperature -40.0 - 40.0 °C
24.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
CTE, linear, Transverse to Flow 45.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
25.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
45.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
25.0 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 196 °C
385 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
196 °C

@Thickness 3.20 mm
385 °F

@Thickness 0.126 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 149 °C
300 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
156 °C

@Thickness 3.20 mm
313 °F

@Thickness 0.126 in
unannealed; ASTM D648