SABIC Innovative Plastics LNP THERMOCOMP PF006U PA 6 (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP PF006U PA 6 (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
UV stabilized, 30% glass fibre reinforced Polyamide 6 injection moulding resin.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.36 g/cc | 0.0491 lb/in³ | ISO 1183 |
| Moisture Absorption | 1.80 % | 1.80 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 6.5 % | 6.5 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0040 cm/cm | 0.0020 - 0.0040 in/in | on Tensile Bar; SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell L | 112 | 112 | ISO 2039-2 |
| Tensile Strength at Break | 160 MPa | 23200 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 3.6 % | 3.6 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 9.50 GPa | 1380 ksi | 1 mm/min; ISO 527 |
| Flexural Strength | 230 MPa | 33400 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 8.00 GPa | 1160 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 11.0 kJ/m² | 5.23 ft-lb/in² | 80*10*4; ISO 180/1A |
| 9.00 kJ/m² @Temperature -40.0 °C |
4.28 ft-lb/in² @Temperature -40.0 °F |
80*10*4; ISO 180/1A | |
| 10.0 kJ/m² @Temperature -20.0 °C |
4.76 ft-lb/in² @Temperature -4.00 °F |
80*10*4; ISO 180/1A | |
| Charpy Impact Unnotched | 9.00 J/cm² | 42.8 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eU |
| 7.50 J/cm² @Temperature -30.0 °C |
35.7 ft-lb/in² @Temperature -22.0 °F |
Edgew 80*10*4 sp=62mm; ISO 179/1eU | |
| Charpy Impact, Notched | 1.10 J/cm² | 5.23 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| 0.900 J/cm² @Temperature -30.0 °C |
4.28 ft-lb/in² @Temperature -22.0 °F |
Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 25.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
13.9 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 85.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
47.2 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Thermal Conductivity | 0.330 W/m-K | 2.29 BTU-in/hr-ft²-°F | ISO 8302 |
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| Vicat Softening Point | 215 °C | 419 °F | Rate B/50; ISO 306 |
| 215 °C | 419 °F | Rate B/120; ISO 306 | |
| Flammability, UL94 | HB @Thickness 0.750 mm |
HB @Thickness 0.0295 in |
UL 94 by SABIC-IP |
| Oxygen Index | 25 % | 25 % | ISO 4589 |
| Glow Wire Test | 650 °C @Thickness 2.00 mm |
1200 °F @Thickness 0.0787 in |
IEC 60695-2-12 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+16 ohm-cm | >= 1.00e+16 ohm-cm | IEC 60093 |
| Surface Resistance | >= 1.00e+16 ohm | >= 1.00e+16 ohm | ROA; IEC 60093 |
| Dielectric Constant | 3.4 @Frequency 1.00e+6 Hz |
3.4 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 3.6 @Frequency 50.0 - 60.0 Hz |
3.6 @Frequency 50.0 - 60.0 Hz |
IEC 60250 | |
| Dielectric Strength | 20.0 kV/mm @Thickness 3.20 mm |
508 kV/in @Thickness 0.126 in |
in oil; IEC 60243-1 |
| Dissipation Factor | 0.0061 @Frequency 50.0 - 60.0 Hz |
0.0061 @Frequency 50.0 - 60.0 Hz |
IEC 60250 |
| 0.016 @Frequency 1.00e+6 Hz |
0.016 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| Comparative Tracking Index | >= 375 V | >= 375 V | IEC 60112 |
| 500 V | 500 V | IEC 60112 |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Wire & Cable JAL110A Natural Polyvinyl Chloride, Flexible (PVC, Flexible)
- MV Labs I860 H5IO6 Periodic acid
- SABIC Innovative Plastics Cycoloy® C3650 PC+ABS (Asia Pacific)
- Karina 65/200 Clear PVC Compound
- Solvay Specialty Polymers Catalyst CT 0552/09 Polyolefin
- Teknor Apex Telcar® TL-2580F Thermoplastic Elastomer
- DSM Akulon® Ultraflow™ K-FHG6 Nylon 6-30% Glass Reinforced (European Grade) (Cond)
- Epoxy Technology EPO-TEK® H35-175MPT Electrically Conductive, Silver Epoxy
- E-Polymers SEPAZ® N3040ST Nanoclay 4% Super Toughness Nano Composite Resin
- SABIC Innovative Plastics LNP VERTON MV008SXP PP (Europe-Africa-Middle East)
Copyright © lookpolymers.com All Rights Reserved