Borealis Bormed™ RD804CF Polypropylene Random Copolymer

Category	Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene Copolymer
Manufacturer	Borealis
Trade Name	Bormed™
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Borealis Bormed™ RD804CF Polypropylene Random Copolymer.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Bormed™ RD804CF is a random copolymer. This grade is suitable for the manufacturing of unoriented films on chill roll processes. Applications Bormed™ RD804CF is recommended for packaging for medical devices, and medical applications. Additives: Bormed™ RD804CF contains no slip, antiblock, antistatic additives or nucleating additives.Information provided by Borealis AG

Physical Properties	Metric	English	Comments
Density	0.905 g/cc	0.0327 lb/in³	base resin; ISO 1183
Melt Flow	8.0 g/10 min @Load 2.16 kg, Temperature 230 °C	8.0 g/10 min @Load 4.76 lb, Temperature 446 °F	ISO 1133

Mechanical Properties	Metric	English	Comments
Tensile Modulus	0.550 GPa	79.8 ksi	MD/TD; ISO 527-3
Flexural Modulus	1.00 GPa	145 ksi	50% humidity; ISO 178
Dart Drop, Total Energy	17.0 J @Thickness 0.0500 mm	12.5 ft-lb @Thickness 0.00197 in	1000N; ISO 4465-2
Film Tensile Strength at Break, MD	40.0 MPa	5800 psi	ISO 527-3
Film Tensile Strength at Break, TD	35.0 MPa	5080 psi	ISO 527-3

Thermal Properties	Metric	English	Comments
Melting Point	150 °C	302 °F	DSC; ISO 3146
Deflection Temperature at 0.46 MPa (66 psi)	70.0 °C	158 °F	ISO 75-2
Vicat Softening Point	139 °C @Load 1.02 kg	282 °F @Load 2.25 lb	A50; ISO 306

Optical Properties	Metric	English	Comments
Haze	<= 2.0 %	<= 2.0 %	ASTM D1003
Gloss	>= 130 %	>= 130 %	20° of arc; ASTM D2457

Users viewing this material also viewed the following: