SABIC Innovative Plastics LNP THERMOCOMP JF004LZ PES
| Category | Polymer , Thermoplastic , Polyethersulfone (PES) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP JF004LZ PES.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Thermocomp* JF004LZ is a compound based on PES containing 20% Glass Fiber. Added features include: Extrusion Grade, Low Extractible.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.54 g/cc | 1.54 g/cc | ASTM D792 |
| Density | 1.54 g/cc | 0.0556 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.340 % | 0.340 % | 50% RH, 24 hrs; ASTM D570 |
| 0.760 % | 0.760 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0050 cm/cm @Time 86400 sec |
0.0030 - 0.0050 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0060 - 0.0080 cm/cm @Time 86400 sec |
0.0060 - 0.0080 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 105 MPa | 15200 psi | 5 mm/min; ISO 527 |
| 107 MPa | 15500 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 2.4 % | 2.4 % | Type I, 5 mm/min; ASTM D638 |
| 2.7 % | 2.7 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 6.83 GPa | 991 ksi | 1 mm/min; ISO 527 |
| 7.28 GPa | 1060 ksi | 5 mm/min; ASTM D638 | |
| Flexural Strength | 156 MPa | 22600 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 6.13 GPa | 889 ksi | 2 mm/min; ISO 178 |
| 6.46 GPa | 937 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.520 J/cm | 0.974 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 5.05 J/cm | 9.46 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 28.0 kJ/m² | 13.3 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 16.0 J @Temperature 23.0 °C |
11.8 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 3.00 J | 2.21 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 31.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
17.2 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 40.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
22.2 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 224 °C | 435 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 223 °C @Thickness 3.20 mm |
433 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 219 °C | 426 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 218 °C @Thickness 3.20 mm |
424 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- MV Labs SM880 Sm(OH)3.xH2O Samarium hydroxide hydrate
- Polykemi AB POLYfill PPH T8038 Polypropylene Homopolymer, Mineral Reinforced
- SABIC Innovative Plastics LNP COLORCOMP D1000P PC (Asia Pacific)
- Hyosung Topilene HJ541CP PP
- Kinlead HSS13 Normal Grade Heat Sealable Film (thickness: 20 µm)
- Samsung Cheil Industries Starex® NH-0700FX ABS, Unreinforced FR
- Ecomass® 1003ZD95 Tungsten Filled COPA
- ConocoPhillips ANDEROL® FGC 150 Compressor Fluid, Synthetic Food Grade ISO 150
- Arlon 55578XC028 0.028" (0.711 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate
Copyright © lookpolymers.com All Rights Reserved