Tipco Tipcofil® AG 600 - 30% Glass Fiber Reinforced Nylon-6 Compound, with High Heat Stability
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 |
| Manufacturer | Tipco Industries Ltd., India |
| Trade Name | Tipcofil® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Tipco Tipcofil® AG 600 - 30% Glass Fiber Reinforced Nylon-6 Compound, with High Heat Stability.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
30% Glass Reinforced Nylon-6 CompoundApplications: General PurposeProcessing: Injection MoldingInformation provided by the Manufacturer, Tipco Industries Ltd.,
India.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.37 g/cc | 0.0495 lb/in³ | ASTM D792 |
| Water Absorption | 1.1 % | 1.1 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0050 cm/cm | 0.0050 in/in | ASTM D955 |
| Melt Flow | 10 g/10 min | 10 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 155 MPa | 22500 psi | ASTM D638 |
| Elongation at Break | >= 4.0 % | >= 4.0 % | ASTM D638 |
| Flexural Yield Strength | 210 MPa | 30500 psi | ASTM D790 |
| Flexural Modulus | 7.50 GPa | 1090 ksi | ASTM D790 |
| Izod Impact, Notched (ISO) | 9.00 kJ/m² | 4.28 ft-lb/in² | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 210 °C | 410 °F | ASTM D648 |
| Vicat Softening Point | 215 °C | 419 °F | ASTM D1525 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 260 °C | 500 °F | |
| Rear Barrel Temperature | 245 °C | 473 °F | |
| Middle Barrel Temperature | 255 °C | 491 °F | |
| Front Barrel Temperature | 265 °C | 509 °F | |
| Nozzle Temperature | 260 °C | 500 °F | |
| Mold Temperature | 100 °C | 212 °F | |
| Drying Temperature | 85.0 °C | 185 °F |
Users viewing this material also viewed the following:
- Nye Lubricants 132DC (SO) Synthetic Oil
- Samsung Cheil Industries Starex® SF-0950S MABS, Unreinforced Scratch Resistant
- SABIC Innovative Plastics LNP STAT-KON AE002 ABS
- Struktol STRUKSILON 8007 Silicone Stabilizer for PU-Rigid Foam
- A. Schulman LP479-01 High-Density Polyethylene Homopolymer
- Tra-Con Tra-Bond 862-12
- C.O.I.M. EXTER S® S 111 B Orthophthalic Resin
- SABIC Innovative Plastics LNP LUBRICOMP GFL36L PSU
- Polimeri Europa SINKRAL L320 ABS (discontinued **)
- Solvay RHODAPHOSE® TETRA BENZYL PYROPHOSPHATE Phosphorus Derivative
Copyright © lookpolymers.com All Rights Reserved