LG Chemical LUMILOY GP2300 Injection Molding Grade, General Purpose 30% Glass Reinforced PPE
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polyphenylene Ether, 30% Glass Filled |
| Manufacturer | LG Chemical |
| Trade Name | LUMILOY |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical LUMILOY GP2300 Injection Molding Grade, General Purpose 30% Glass Reinforced PPE.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
NSF Certified for KA02 and E2035. Noted for High Impact Strength, and Hydrolytic Stability. Uses include electric/electronic parts and water pump Housing or impellers and other parts with water contact.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.28 g/cc | 0.0462 lb/in³ | ASTM D792 |
| Melt Flow | 9.5 g/10 min @Load 5.00 kg, Temperature 280 °C |
9.5 g/10 min @Load 11.0 lb, Temperature 536 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 121 MPa @Thickness 3.20 mm |
17500 psi @Thickness 0.126 in |
ASTM D638 |
| Elongation at Break | 7.0 % @Thickness 3.17 mm |
7.0 % @Thickness 0.125 in |
ASTM D638 |
| Flexural Strength | 172 MPa @Thickness 3.20 mm |
24900 psi @Thickness 0.126 in |
ASTM D790 |
| Flexural Modulus | 6.37 GPa @Thickness 3.20 mm |
925 ksi @Thickness 0.126 in |
ASTM D790 |
| Izod Impact, Notched | 1.27 J/cm @Thickness 3.20 mm |
2.39 ft-lb/in @Thickness 0.126 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 135 °C @Thickness 3.20 mm |
275 °F @Thickness 0.126 in |
Unannealed; ASTM D648 |
| Vicat Softening Point | 148 °C | 298 °F | Rate B/50; ASTM D1525 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 260 - 300 °C | 500 - 572 °F | |
| Middle Barrel Temperature | 270 - 310 °C | 518 - 590 °F | |
| Front Barrel Temperature | 270 - 310 °C | 518 - 590 °F | |
| Nozzle Temperature | 270 - 310 °C | 518 - 590 °F | |
| Mold Temperature | 70.0 - 110 °C | 158 - 230 °F | |
| Drying Temperature | 90 - 100 °C | 190 - 212 °F | |
| Dry Time | 4 - 5 hour | 4 - 5 hour | |
| Moisture Content | >= 0.03 % | >= 0.03 % |
Users viewing this material also viewed the following:
- Quantum Composites LYTEX® 4181 55% Carbon Fiber Reinforced Epoxy SMC
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 30 PHR N990 Filler
- Techmer ES Luriblend® PA6/6 CF30 TS15 BK 30% Carbon Filled
- Schmolz + Bickenbach UGIMA® 303 HD Stainless Steel Bar
- Dow Corning SILASTIC® LS 5-8761 FLUOROSILICONE RUBBER BASE
- EMS-Grivory Grivory® L 25 NZ ESD PA12
- Eurostar Starpylen MF004S PP, 20% Glass Fiber Filled, Injection Molded
Copyright © lookpolymers.com All Rights Reserved