SABIC Innovative Plastics LNP STAT-KON RE0029 PA 66

Category Polymer , Thermoplastic , Nylon , Nylon 66
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP STAT-KON
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP STAT-KON RE0029 PA 66.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* STAT-KON* RE0029 is a compound based on Nylon 66 resin containing 10% Carbon Fiber. Added features of this material include: Electrically Conductive, Flame Retardant.
Physical Properties Metric English Comments
Density 1.46 g/cc
0.0527 lb/in³
ASTM D792
1.46 g/cc
0.0527 lb/in³
ISO 1183
Moisture Absorption 0.400 %
0.400 %
50% RH, 24 hrs; ASTM D570
Linear Mold Shrinkage, Flow 0.0040 cm/cm

@Time 86400 sec
 0.0040 in/in

@Time 24.0 hour
 ASTM D955
0.0044 cm/cm

@Time 86400 sec
 0.0044 in/in

@Time 24.0 hour
 ISO 294
Linear Mold Shrinkage, Transverse 0.011 cm/cm

@Time 86400 sec
 0.011 in/in

@Time 24.0 hour
 ASTM D955
0.011 cm/cm

@Time 86400 sec
 0.011 in/in

@Time 24.0 hour
 ISO 294
Mechanical Properties Metric English Comments
Tensile Strength at Break 126 MPa
18300 psi
ISO 527
131 MPa
19000 psi
ASTM D638
Tensile Strength, Yield 126 MPa
18300 psi
ISO 527
131 MPa
19000 psi
ASTM D638
Elongation at Break 1.6 %
1.6 %
ISO 527
1.7 %
1.7 %
ASTM D638
Elongation at Yield 1.6 %
1.6 %
ISO 527
1.7 %
1.7 %
ASTM D638
Tensile Modulus 10.21 GPa
1481 ksi
1 mm/min; ISO 527
11.03 GPa
1600 ksi
50 mm/min; ASTM D638
Flexural Strength 179 MPa
26000 psi
ASTM D790
186 MPa
27000 psi
ISO 178
Flexural Modulus 8.27 GPa
1200 ksi
ASTM D790
9.00 GPa
1310 ksi
ISO 178
Izod Impact, Notched 0.320 J/cm
0.599 ft-lb/in
ASTM D256
Izod Impact, Unnotched 13.29 J/cm
24.90 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 4.00 kJ/m²
1.90 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 24.0 kJ/m²
11.4 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 5.00 J
3.69 ft-lb
Instrumented Impact Energy @ peak; ASTM D3763
Impact Test 3.00 J
2.21 ft-lb
Multiaxial Impact; ISO 6603
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 64.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 35.6 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
64.8 µm/m-°C

@Temperature -40.0 - 40.0 °C
 36.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
CTE, linear, Transverse to Flow 25.2 µm/m-°C

@Temperature -40.0 - 40.0 °C
 14.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
26.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 14.4 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 253 °C
487 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
256 °C

@Thickness 3.20 mm
 493 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 233 °C
451 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
238 °C

@Thickness 3.20 mm
 460 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Electrical Properties Metric English Comments
Surface Resistance 100 - 1.00e+6 ohm
100 - 1.00e+6 ohm
ASTM D257