SABIC Innovative Plastics LNP STAT-KON RD000I PA 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP STAT-KON RD000I PA 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* STAT-KON* RD000I is a compound based on Nylon 66 resin containing Carbon Powder. Added features of this material include: Electrically Conductive, High Impact.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.15 g/cc | 1.15 g/cc | ASTM D792 |
| Density | 1.15 g/cc | 0.0415 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.490 % | 0.490 % | 50% RH, 24 hrs; ASTM D570 |
| 0.730 % | 0.730 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | >= 0.020 cm/cm @Time 86400 sec |
>= 0.020 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.020 - 0.040 cm/cm @Time 86400 sec |
0.020 - 0.040 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 41.0 MPa | 5950 psi | Type I, 5 mm/min; ASTM D638 |
| 41.0 MPa | 5950 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 18 % | 18 % | Type I, 5 mm/min; ASTM D638 |
| 18 % | 18 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 2.12 GPa | 307 ksi | 50 mm/min; ASTM D638 |
| 2.19 GPa | 318 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 62.0 MPa | 8990 psi | ISO 178 |
| Flexural Modulus | 1.92 GPa | 278 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 2.02 GPa | 293 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 1.37 J/cm | 2.57 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 18.1 J/cm | 33.9 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 14.0 kJ/m² | 6.66 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 155 kJ/m² | 73.8 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 16.0 J @Temperature 23.0 °C |
11.8 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 20.0 J | 14.8 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 109 µm/m-°C @Temperature -30.0 - 30.0 °C |
60.6 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 118 µm/m-°C @Temperature -30.0 - 30.0 °C |
65.6 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Thermal Conductivity | 2.80 W/m-K | 19.4 BTU-in/hr-ft²-°F | ASTM E 1530 |
| Deflection Temperature at 0.46 MPa (66 psi) | 191 °C | 376 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 206 °C @Thickness 3.20 mm |
403 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 68.0 °C | 154 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 71.0 °C @Thickness 3.20 mm |
160 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 100 - 1.00e+6 ohm | 100 - 1.00e+6 ohm | ASTM D257 |
Users viewing this material also viewed the following:
- Mytex Polymers AN16L-53 Polypropylene, Compounded
- Cookson Group Plaskon® 3100LS Mineral Filled Conventional Encapsulant (discontinued **)
- DuPont Performance Polymers Zytel® ST7301 BK356 Nylon 6 (Unverified Data**)
- Techmer ES Luriblend® PA6/6 GF33 TS15 33% Glass Filled
- SABIC Innovative Plastics LNP THERMOCOMP QF008 PA6.10
- Silikony Polskie Polsil E5 Silicone Emulsion
- Covestro Bayblend® T88-2N Polycarbonate + ABS, 10% Glass Filled
- ExxonMobil LDPE LD 150BW Low Density Polyethylene Resin
- Arlon CuClad 6700 Bonding Film
- M. Holland Company IS325 Polystyrene, High Impact (discontinued **)
Copyright © lookpolymers.com All Rights Reserved