SABIC Innovative Plastics LNP STAT-KON KS302 Acetal Copoly (Asia Pacific)
| Category | Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, Unreinforced |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP STAT-KON KS302 Acetal Copoly (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Stat-kon* KS302 is a compound based on Acetal Copolymer resin containing Stainless Steel.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.50 g/cc | 0.0542 lb/in³ | ASTM D792 |
| 1.50 g/cc | 0.0542 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.200 % | 0.200 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | >= 0.020 cm/cm @Time 86400 sec |
>= 0.020 in/in @Time 24.0 hour |
ASTM D955 |
| 0.025 cm/cm @Time 86400 sec |
0.025 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.025 cm/cm @Time 86400 sec |
0.025 in/in @Time 24.0 hour |
ISO 294 |
| 0.020 - 0.040 cm/cm @Time 86400 sec |
0.020 - 0.040 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 48.0 MPa | 6960 psi | ASTM D638 |
| 52.0 MPa | 7540 psi | ISO 527 | |
| Tensile Strength, Yield | 51.0 MPa | 7400 psi | ASTM D638 |
| 52.0 MPa | 7540 psi | ISO 527 | |
| Elongation at Break | 12.9 % | 12.9 % | ISO 527 |
| 38.7 % | 38.7 % | ASTM D638 | |
| Elongation at Yield | 8.4 % | 8.4 % | ISO 527 |
| 9.0 % | 9.0 % | ASTM D638 | |
| Tensile Modulus | 2.75 GPa | 399 ksi | 50 mm/min; ASTM D638 |
| 3.03 GPa | 439 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 65.0 MPa | 9430 psi | ISO 178 |
| Flexural Modulus | 2.06 GPa | 299 ksi | ASTM D790 |
| 4.30 GPa | 624 ksi | ISO 178 | |
| Izod Impact, Notched | 0.420 J/cm | 0.787 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 8.81 J/cm | 16.5 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 49.0 kJ/m² | 23.3 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 5.00 J | 3.69 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 1.00 J | 0.738 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 118 µm/m-°C @Temperature -40.0 - 40.0 °C |
65.6 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 119 µm/m-°C @Temperature -40.0 - 40.0 °C |
66.1 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| CTE, linear, Transverse to Flow | 108 µm/m-°C @Temperature -40.0 - 40.0 °C |
60.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 108 µm/m-°C @Temperature -40.0 - 40.0 °C |
60.0 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 150 °C | 302 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 152 °C @Thickness 3.20 mm |
306 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 90.0 °C | 194 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 92.0 °C @Thickness 3.20 mm |
198 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Nyco M1250 ES WOLLASTOCOAT® Wollastonite
- ExxonMobil Escorene® LL-3105 LLDPE/Hexene Premium Film Resin, Tough (discontinued **)
- Huntsman IROGRAN® A 65 P 4324 N TPU-Polyether
- Intercontinental Polymers Deniers 3-10 Polyester Staple Fibers, Deniers 3 - 10
- Lanxess Durethan® BKV 215 H2.0 901510 Copolyamide, 15% Glass Fiber
- Silberline Silvex® 335-20-D
- Styron DGF080.00 ESU Polypropylene
- Eagle Brass 725 Copper Nickel Tin, Extra Hard
- BCC Products BC 8870 Polyurethane Elastomer
Copyright © lookpolymers.com All Rights Reserved