- Materion Beryllium Copper Alloy 190 Strip; AM (TM00) Temper (UNS C17200)
Materion Beryllium Copper Alloy 190 Strip; AM (TM00) Temper (UNS C17200)
| Category | Metal , Nonferrous Metal , Beryllium Alloy , Copper Alloy |
| Manufacturer | Materion Corporation (former Brush Wellman) |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Materion Beryllium Copper Alloy 190 Strip; AM (TM00) Temper (UNS C17200).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Treatment required for max strength: Mill HardenedStress Relaxation-% Stress Remaining after 1000 hrs @ 100°C: 97%Stress Relaxation after 1000 hrs @ 200°C: 67%Formability Ratio, 90° Bend, Radius/Thickness (Good Way): 0Formability Ratio (bad Way): 0Superficial Hardness: 30N 37-44Tabulated properties apply to products after age hardening. Information supplied by Brush Wellman.Brush Engineered Materials Inc. changed its name to Materion Corporation in March 2011.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 8.36 g/cc | 0.302 lb/in³ |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell B | >= 95 | >= 95 | |
| Hardness, Rockwell C | <= 23 | <= 23 | |
| Hardness, Vickers | 210 - 251 | 210 - 251 | |
| Tensile Strength, Ultimate | 680 - 760 MPa | 98600 - 110000 psi | |
| Tensile Strength, Yield | 480 - 660 MPa | 69600 - 95700 psi | |
| Elongation at Break | 16 - 30 % | 16 - 30 % | |
| Modulus of Elasticity | 131 GPa | 19000 ksi | |
| Fatigue Strength | 280 - 310 MPa @# of Cycles 1.00e+8 |
40600 - 45000 psi @# of Cycles 1.00e+8 |
Reverse Bending (R=1) |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 17.0 µm/m-°C @Temperature 20.0 - 200 °C |
9.44 µin/in-°F @Temperature 68.0 - 392 °F |
|
| Thermal Conductivity | 105 W/m-K | 729 BTU-in/hr-ft²-°F | |
| Melting Point | 870 - 980 °C | 1600 - 1800 °F | |
| Solidus | 870 °C | 1600 °F | |
| Liquidus | 980 °C | 1800 °F |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Beryllium, Be | 1.8 - 2.0 % | 1.8 - 2.0 % | |
| Co + Ni | >= 0.20 % | >= 0.20 % | |
| Co + Ni + Fe | <= 0.60 % | <= 0.60 % | |
| Copper, Cu | 98 % | 98 % | as balance |
| Lead, Pb | <= 0.020 % | <= 0.020 % |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 0.00000610 - 0.0000101 ohm-cm | 0.00000610 - 0.0000101 ohm-cm | 17-28% IACS Conductivity |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® LUX7436C PC COPOLYMER
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 10 PHR N339 Filler
- Karina E 42/261-GEN Dark Red MBATCH (SP31543) for PVC
- Huntsman IROGRAN® A 95 K 4977 TPU-High Temperature Performance
- SABIC Innovative Plastics NORYL EZ250 PPE+PS
- Arlon 51271R037 0.037" Uncured Silicone Rubber with Fiberglass Substrate
- Quadrant EPP Quicksilver® UHMW-PE Premium Truck Lining (ASTM Product Data Sheet)
- ExxonMobil Paxon™ AS55-003 Blow Molding Resin (discontinued **)
- A. Schulman POLYFORT™ FPP 1200X High Flow, Calcium Carbonate Fortified Homopolymer Polypropylene
Copyright © lookpolymers.com All Rights Reserved