SABIC Innovative Plastics LNP LUBRILOY U2000A PPA (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyphthalamide (PPA) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP Lubriloy |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRILOY U2000A PPA (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Lubriloy* U2000A is a compound based on Polyphthalamide resin containing Proprietary Lubricant. Added features of this material include: Internally Lubricated.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in³ | ASTM D792 |
| 1.14 g/cc | 0.0412 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.300 % | 0.300 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.016 - 0.018 cm/cm @Time 86400 sec |
0.016 - 0.018 in/in @Time 24.0 hour |
ASTM D955 |
| 0.017 cm/cm @Time 86400 sec |
0.017 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.016 - 0.018 cm/cm @Time 86400 sec |
0.016 - 0.018 in/in @Time 24.0 hour |
ASTM D955 |
| 0.017 cm/cm @Time 86400 sec |
0.017 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 78.0 MPa | 11300 psi | ISO 527 |
| 81.0 MPa | 11700 psi | ASTM D638 | |
| Tensile Strength, Yield | 78.0 MPa | 11300 psi | ISO 527 |
| 81.0 MPa | 11700 psi | ASTM D638 | |
| Elongation at Break | 3.4 % | 3.4 % | ISO 527 |
| 3.6 % | 3.6 % | ASTM D638 | |
| Elongation at Yield | 3.4 % | 3.4 % | ISO 527 |
| 3.6 % | 3.6 % | ASTM D638 | |
| Tensile Modulus | 3.44 GPa | 499 ksi | 50 mm/min; ASTM D638 |
| 3.53 GPa | 512 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 109 MPa | 15800 psi | ISO 178 |
| Flexural Modulus | 2.75 GPa | 399 ksi | ASTM D790 |
| 2.90 GPa | 421 ksi | ISO 178 | |
| Izod Impact, Notched | 0.580 J/cm | 1.09 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 13.45 J/cm | 25.20 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | 80*10*4; ISO 180/1A |
| Dart Drop, Total Energy | 4.00 J | 2.95 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 16.0 J | 11.8 ft-lb | Multiaxial Impact; ISO 6603 |
| Coefficient of Friction, Dynamic | 0.22 | 0.22 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.22 | 0.22 | ASTM D3702 Modified |
| K (wear) Factor | 40.3 x 10-8 mm³/N-M | 20.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 70.2 µm/m-°C @Temperature -40.0 - 40.0 °C |
39.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 71.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
39.4 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 70.2 µm/m-°C @Temperature -40.0 - 40.0 °C |
39.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 71.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
39.4 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 183 °C | 361 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 163 °C @Thickness 3.20 mm |
325 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 103 °C | 217 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 106 °C @Thickness 3.20 mm |
223 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Teknor Apex Chemlon® 109 Nylon 66, Impact Grade
- Shin-Etsu Silicones KSG-15 Fluid
- Teknor Apex Vidux® 100-1A Polyvinyl Chloride, Flexible
- A. Schulman PP 1259 Polypropylene Medium Impact Polypropylene
- Dow SARAN WRAP™ 3 Plastic Film
- 3M 9672LE Adhesive Transfer Tapes with Adhesive 300LSE
- AK Steel ASTM A 1011, Grade 55 Hot Rolled Carbon Steel, Structural Steel (SS)
- Carpenter Custom 450® Stainless Steel, Condition H1050 (Age Hardened 566°C)
- Latrobe LSS™ S1 Shock-Resisting Tool Steel (ASTM S1)
Copyright © lookpolymers.com All Rights Reserved