SABIC Innovative Plastics LNP LUBRICOMP SG004 PA12 (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Nylon , Nylon 12 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP SG004 PA12 (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* LUBRICOMP* SG004 is a compound based on PA 12 resin containing Graphite. Added features include: Internally Lubricated.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in³ | ISO 1183 |
| Water Absorption | 0.14 % @Time 86400 sec |
0.14 % @Time 24.0 hour |
ISO 62-1 |
| Linear Mold Shrinkage, Flow | 0.011 cm/cm | 0.011 in/in | SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 43.0 MPa | 6240 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 6.6 % | 6.6 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 2.40 GPa | 348 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 66.0 MPa | 9570 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 2.30 GPa | 334 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² | 1.90 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 25.0 kJ/m² | 11.9 ft-lb/in² | 80*10*4; ISO 180/1U |
| Coefficient of Friction, Dynamic | 0.41 | 0.41 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.31 | 0.31 | ASTM D3702 Modified |
| K (wear) Factor | 898 x 10-8 mm³/N-M | 446 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 72.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
40.0 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 90.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
50.0 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 147 °C | 297 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 74.0 °C | 165 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
Users viewing this material also viewed the following:
- PolyOne Geon™ HC 8210 Polyvinyl Chloride, Rigid (PVC, Rigid)
- Indium Corp. Indalloy 160 Tin Solder Alloy
- Karina E 786-10/332-IS-RG Compound PVC White
- LG Chemical TR552 MABS, Transparency, High Impact, Chemical Resistance
- DuPont Elvaloy® 4170 Reactive Ethylene Terpolymer (RET)
- TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, Hardness 80A, Non-Black Peroxide Cure
- Eagle Brass 511 Phosphor Bronzes 4%, Extra Hard
- Chevron Phillips MarFlex® 1125 Polyethylene; LDPE
- Beijing Chemical Industry KAIFA® 302-G0 PBT Resin
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 70 PHR N220 (ISAF) Filler
Copyright © lookpolymers.com All Rights Reserved