SABIC Innovative Plastics LNP LUBRICOMP RN001S PA 66 (Asia Pacific)
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP RN001S PA 66 (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Lubricomp* RN001S is a compound based on Nylon 66 resin containing MOS2. Added features of this material include: Internally Lubricated, Heat Stabilized.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.16 g/cc | 0.0419 lb/in³ | ASTM D792 |
| 1.17 g/cc | 0.0423 lb/in³ | ISO 1183 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 69.0 MPa | 10000 psi | ISO 527 |
| 84.0 MPa | 12200 psi | ASTM D638 | |
| Tensile Strength, Yield | 69.0 MPa | 10000 psi | ISO 527 |
| 84.0 MPa | 12200 psi | ASTM D638 | |
| Elongation at Break | 3.8 % | 3.8 % | ASTM D638 |
| 42.2 % | 42.2 % | ISO 527 | |
| Elongation at Yield | 2.0 % | 2.0 % | ISO 527 |
| 2.9 % | 2.9 % | ASTM D638 | |
| Tensile Modulus | 3.91 GPa | 567 ksi | 1 mm/min; ISO 527 |
| 4.13 GPa | 599 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 107 MPa | 15500 psi | ISO 178 |
| Flexural Modulus | 3.40 GPa | 493 ksi | ISO 178 |
| 3.44 GPa | 499 ksi | ASTM D790 | |
| Izod Impact, Notched | 0.260 J/cm | 0.487 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 11.1 J/cm | 20.8 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 2.00 kJ/m² | 0.952 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 53.0 kJ/m² | 25.2 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 2.00 J | 1.48 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Coefficient of Friction, Dynamic | 0.75 | 0.75 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.55 | 0.55 | ASTM D3702 Modified |
| K (wear) Factor | 207 x 10-8 mm³/N-M | 103 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 223 °C | 433 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 231 °C @Thickness 3.20 mm |
448 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 76.0 °C @Thickness 3.20 mm |
169 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- DuPont™ Dartek® O-401 Nylon 6,6 Oriented Film, 15 µm Thickness (discontinued **)
- BASF Capron® 5233G 33% Glass-Filled Nylon 66 (Dry) (discontinued **)
- Formosa Plastics Formolon® 622R PVC
- DuPont Performance Polymers Delrin® 500PE NC010A Acetal Homopolymer
- BASF Ultradur B 4040 G10 BK5110 50% Glass Filled PBT
- Arkema Group EVATANE® 28-03 Copolymer Ethylene - Vinyl Acetate
- Samsung Cheil Industries Infino® VB-5300GS PBT, Glass Filled FR
- Lendell Manufacturing Prepol Pre Polymer
- Westlake Hifor LT74107-F Polyethylene Film, Using Energx Technology Services (discontinued **)
Copyright © lookpolymers.com All Rights Reserved