SABIC Innovative Plastics LNP LUBRICOMP RFI12 PA 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP RFI12 PA 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* LUBRICOMP* RFI12 is a compound based on Nylon 66 resin containing 10% Glass Fiber, 2% Silicone. Added feature of this material is: Wear Resistant.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.25 g/cc | 1.25 g/cc | ASTM D792 |
| Density | 1.25 g/cc | 0.0452 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.980 % | 0.980 % | 50% RH, 24 hrs; ASTM D570 |
| 1.50 % | 1.50 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0090 - 0.020 cm/cm @Time 86400 sec |
0.0090 - 0.020 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.030 cm/cm @Time 86400 sec |
0.010 - 0.030 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 107 MPa | 15500 psi | 5 mm/min; ISO 527 |
| 114 MPa | 16500 psi | Type I, 5 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 107 MPa | 15500 psi | 5 mm/min; ISO 527 |
| 114 MPa | 16500 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 2.6 % | 2.6 % | 5 mm/min; ISO 527 |
| 2.8 % | 2.8 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 2.6 % | 2.6 % | 5 mm/min; ISO 527 |
| 2.8 % | 2.8 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 5.26 GPa | 763 ksi | 1 mm/min; ISO 527 |
| 5.50 GPa | 798 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 155 MPa | 22500 psi | ISO 178 |
| 165 MPa | 23900 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Yield Strength | 166 MPa | 24100 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 4.43 GPa | 643 ksi | 2 mm/min; ISO 178 |
| 4.78 GPa | 693 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.400 J/cm | 0.749 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 4.62 J/cm | 8.66 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² | 1.90 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 27.0 kJ/m² | 12.8 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 5.00 J @Temperature 23.0 °C |
3.69 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 1.00 J | 0.738 ft-lb | Multiaxial Impact; ISO 6603 |
| Coefficient of Friction, Dynamic | 0.47 | 0.47 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.43 | 0.43 | ASTM D3702 Modified |
| K (wear) Factor | 524 x 10-8 mm³/N-M | 260 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 255 °C | 491 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 257 °C @Thickness 3.20 mm |
495 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 236 °C | 457 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 241 °C @Thickness 3.20 mm |
466 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- ITW Devcon Metal Repair Titanium Putty, Grey
- LATI Laticonther 80 CPG/700 PPS, Glass Fiber Reinforced
- Seals Eastern 5243 Neoprene / Chloroprene
- STAR Thermoplastic Alloys & Rubbers StarFlex® P 7350-9000 TPE
- SABIC Innovative Plastics LNP THERMOTUF WF006I PBT
- Sumitomo Chemical ESPOLEX® UT461A Thermoplastic Elastomer
- Master Bond UV15-42C One Component, Optically Clear, Tough UV Curable System
- ExxonMobil HD 6719.17 Injection Molding Resin
- Colorite Polymers 8090C General Purpose Vinyl Compound
- Fainplast Compounds PH 55 Flexible PVC, Transparent Extrusion
Copyright © lookpolymers.com All Rights Reserved