SABIC Innovative Plastics LNP LUBRICOMP OCP36 PPS
| Category | Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP OCP36 PPS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* LUBRICOMP* OCP36 is a compound based on Polyphenylene Sulfide resin containing 30% Carbon Fiber, 15% PTFE/Silicone. Added features of this grade include: Wear Resistant, Bearing Grade, Electrically Conductive.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.51 g/cc | 0.0546 lb/in³ | ASTM D792 |
| 1.54 g/cc | 0.0556 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.0200 % | 0.0200 % | 50% RH, 24 hrs; ASTM D570 |
| 0.0200 % | 0.0200 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0030 cm/cm @Time 86400 sec |
0.0020 - 0.0030 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0040 - 0.0060 cm/cm @Time 86400 sec |
0.0040 - 0.0060 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 175 MPa | 25400 psi | Type I, 5 mm/min; ASTM D638 |
| 175 MPa | 25400 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 175 MPa | 25400 psi | Type I, 5 mm/min; ASTM D638 |
| 175 MPa | 25400 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 0.40 % | 0.40 % | Flexural Strain, break, 2 mm/min; ISO 178 |
| 1.0 % | 1.0 % | Type I, 5 mm/min; ASTM D638 | |
| 1.0 % | 1.0 % | 5 mm/min; ISO 527 | |
| Elongation at Yield | 1.0 % | 1.0 % | Type I, 5 mm/min; ASTM D638 |
| 1.0 % | 1.0 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 18.14 GPa | 2631 ksi | 50 mm/min; ASTM D638 |
| 28.8 GPa | 4180 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 237 MPa | 34400 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Yield Strength | 237 MPa | 34400 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 21.3 GPa | 3090 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Izod Impact, Notched | 0.530 J/cm | 0.993 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 4.85 J/cm | 9.09 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² | 1.90 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 26.0 kJ/m² | 12.4 ft-lb/in² | 80*10*4; ISO 180/1U |
| Coefficient of Friction, Dynamic | 0.47 | 0.47 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.33 | 0.33 | ASTM D3702 Modified |
| K (wear) Factor | 48.3 x 10-8 mm³/N-M | 24.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 278 °C | 532 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 279 °C @Thickness 3.20 mm |
534 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 266 °C | 511 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 260 °C @Thickness 3.20 mm |
500 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 100 ohm | 100 ohm | ASTM D257 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics LNP COLORCOMP NX05467 PC+ABS
- Poco Graphite AXF-5Q Industrial Grade Graphite
- Mo-Sci Corporation GL-0193 Hollow Glass Spheres
- TSE Industries Thanecure® ZM Activator/Accelerator for Sulfur Curable Polyurethane Rubber
- Loctite® Tak Pak® 7452 Accelerator
- Fainplast Compounds GS 58/O Flexible PVC, Injection Molding for Footwear
- Arlon 510-638R-50 0.008" (0.203 mm) Silicone Rubber Coated Fiberglass
- Arlon CP-427R Silicone Rubber
- Total PPC 3120 MU5 Polypropylene, Heterophasic Copolymer, Automotive