SABIC Innovative Plastics Lexan® FL410 PC

Category Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Lexan®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Lexan® FL410 PC.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Various weight reductions at 0.250: (6.38 mm) wall. Thin wall capability high flexural mod, strength and creep resistant. V-0/5V - 0.157""(3.98 mm).
Physical Properties Metric English Comments
Specific Gravity 1.13 g/cc
1.13 g/cc
foam molded; ASTM D792
1.25 g/cc
1.25 g/cc
ASTM D792
Water Absorption 0.14 %

@Time 86400 sec
 0.14 %

@Time 24.0 hour
 ASTM D570
Moisture Absorption at Equilibrium 0.31 %
0.31 %
ASTM D570
Linear Mold Shrinkage, Flow 0.0040 - 0.0060 cm/cm

@Thickness 6.40 mm
 0.0040 - 0.0060 in/in

@Thickness 0.252 in
 SABIC Method
Mechanical Properties Metric English Comments
Tensile Strength, Yield 50.0 MPa

@Thickness 6.35 mm
 7250 psi

@Thickness 0.250 in
 ASTM D638
Elongation at Break 4.8 %

@Thickness 6.35 mm
 4.8 %

@Thickness 0.250 in
 ASTM D638
Tensile Modulus 3.17 GPa

@Thickness 6.40 mm
 460 ksi

@Thickness 0.252 in
 ASTM D638
Flexural Yield Strength 93.0 MPa
13500 psi
6.4 mm; ASTM D790
Flexural Modulus 3.82 GPa
554 ksi
6.4 mm; ASTM D790
Izod Impact, Unnotched 8.54 J/cm
16.0 ft-lb/in
ASTM D4812
Dart Drop, Total Energy 46.0 J
33.9 ft-lb
SABIC Method
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 32.4 µm/m-°C

@Temperature -40.0 - 95.0 °C
 18.0 µin/in-°F

@Temperature -40.0 - 203 °F
 ASTM E 831
Specific Heat Capacity 1.15 J/g-°C
0.275 BTU/lb-°F
ASTM C351
Deflection Temperature at 0.46 MPa (66 psi) 137 °C

@Thickness 6.40 mm
 279 °F

@Thickness 0.252 in
 unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 132 °C

@Thickness 6.40 mm
 270 °F

@Thickness 0.252 in
 unannealed; ASTM D648
UL RTI, Electrical 80.0 °C
176 °F
UL 746B
UL RTI, Mechanical with Impact 80.0 °C
176 °F
UL 746B
UL RTI, Mechanical without Impact 80.0 °C
176 °F
UL 746B
Flammability, UL94 V-0

@Thickness 2.99 mm
 V-0

@Thickness 0.118 in
 UL 94
5VA

@Thickness 3.81 mm
 5VA

@Thickness 0.150 in
 UL 94
Electrical Properties Metric English Comments
Volume Resistivity 2.40e+17 ohm-cm
2.40e+17 ohm-cm
ASTM D257
Surface Resistance >= 1.10e+17 ohm
>= 1.10e+17 ohm
ASTM D257
Dielectric Constant 2.32

@Frequency 1.00e+6 Hz
 2.32

@Frequency 1.00e+6 Hz
 ASTM D150
2.4

@Frequency 100 Hz
 2.4

@Frequency 100 Hz
 ASTM D150
Dissipation Factor 0.0028

@Frequency 100 Hz
 0.0028

@Frequency 100 Hz
 ASTM D150
0.0081

@Frequency 1.00e+6 Hz
 0.0081

@Frequency 1.00e+6 Hz
 ASTM D150
Arc Resistance 0.00 - 60 sec
0.00 - 60 sec
Tungsten; ASTM D495
Comparative Tracking Index 100 - 175 V
100 - 175 V
UL 746A
High Voltage Arc-Tracking Rate, HVTR >= 150 mm/min
>= 5.91 in/min
UL 746A
Descriptive Properties Value Comments
FOAM - ELECTRICAL 6.4 mm Wt Reduction 20%
FOAM - Flame Class Minimum Density 1g/cm^3
FOAM - IMPACT 6.4 mm Wt Reduction 10%
FOAM - MECHANICAL 6.4 mm Wt Reduction 10%
FOAM - PHYSICAL 6.4mm Wt Reduction 10%
FOAM - THERMAL 6.4mm Wt Reduction 10%