Songhan Plastic Technology Co.,Ltd.
 POLYMER SEARCH

DuPont Performance Polymers Crastin® HR5315HF NC010 Polybutylene Terephthalate (PBT)  (Unverified Data**)&

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 20% Glass Fiber Filled
Manufacturer DuPont Performance Polymers
Trade Name Crastin®
Port Ningbo port,China
Trade Terms EXW, FOB, CFR, CIF
Payment Terms L/C, T/T, PayPal
Download PDF DuPont Performance Polymers Crastin® HR5315HF NC010 Polybutylene Terephthalate (PBT)  (Unverified Data**)&.pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
15% Glass Reinforced Hydrolysis Resistant Polybutylene Terephthalate Crastin HR5315HF is a 15% glass reinforced PBT with high flow (HF) moderately toughened hydrolysis resistant (HR) resin. Excellent balance of properties between terminal pullout and iInformation provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.14 g/cc
0.0412 lb/in³
1.37 g/cc
0.0495 lb/in³
ISO 1183
Water Absorption 0.40 %
<br>@Thickness 2.00 mm
 0.40 %
<br>@Thickness 0.0787 in
 Sim. to ISO 62
Moisture Absorption 0.150 %
<br>@Thickness 2.00 mm
 0.150 %
<br>@Thickness 0.0787 in
 Sim. to ISO 62
Viscosity 55190 cP
<br>@Shear Rate 5000 1/s,<br> Temperature 260 °C
 55190 cP
<br>@Shear Rate 5000 1/s,<br> Temperature 500 °F
 ISO 11403-1 -2
63820 cP
<br>@Shear Rate 5000 1/s,<br> Temperature 250 °C
 63820 cP
<br>@Shear Rate 5000 1/s,<br> Temperature 482 °F
 ISO 11403-1 -2
74630 cP
<br>@Shear Rate 5000 1/s,<br> Temperature 240 °C
 74630 cP
<br>@Shear Rate 5000 1/s,<br> Temperature 464 °F
 ISO 11403-1 -2
167300 cP
<br>@Shear Rate 500 1/s,<br> Temperature 260 °C
 167300 cP
<br>@Shear Rate 500 1/s,<br> Temperature 500 °F
 ISO 11403-1 -2
195800 cP
<br>@Shear Rate 500 1/s,<br> Temperature 250 °C
 195800 cP
<br>@Shear Rate 500 1/s,<br> Temperature 482 °F
 ISO 11403-1 -2
231200 cP
<br>@Shear Rate 500 1/s,<br> Temperature 240 °C
 231200 cP
<br>@Shear Rate 500 1/s,<br> Temperature 464 °F
 ISO 11403-1 -2
Viscosity Test 95 cm³/g
95 cm³/g
ISO 307 1157 1628
Linear Mold Shrinkage, Flow 0.0050 cm/cm
0.0050 in/in
ISO 294-4 2577
Linear Mold Shrinkage, Transverse 0.011 cm/cm
0.011 in/in
ISO 294-4 2577
Mechanical Properties Metric English Comments
Hardness, Rockwell R 115
115
ISO 2039-2
Tensile Strength at Break 95.0 MPa
13800 psi
ISO 527-1/-2
Tensile Stress 9.14 MPa
<br>@Strain 0.550 %,<br> Temperature 150 °C
 1330 psi
<br>@Strain 0.550 %,<br> Temperature 302 °F
 ISO 11403-1 -2
9.58 MPa
<br>@Strain 0.390 %,<br> Temperature 90.0 °C
 1390 psi
<br>@Strain 0.390 %,<br> Temperature 194 °F
 ISO 11403-1 -2
18.33 MPa
<br>@Strain 0.430 %,<br> Temperature 40.0 °C
 2659 psi
<br>@Strain 0.430 %,<br> Temperature 104 °F
 ISO 11403-1 -2
20.5 MPa
<br>@Strain 0.360 %,<br> Temperature 23.0 °C
 2970 psi
<br>@Strain 0.360 %,<br> Temperature 73.4 °F
 ISO 11403-1 -2
22.0 MPa
<br>@Strain 1.71 %,<br> Temperature 150 °C
 3190 psi
<br>@Strain 1.71 %,<br> Temperature 302 °F
 ISO 11403-1 -2
25.93 MPa
<br>@Strain 1.20 %,<br> Temperature 90.0 °C
 3761 psi
<br>@Strain 1.20 %,<br> Temperature 194 °F
 ISO 11403-1 -2
29.54 MPa
<br>@Strain 2.90 %,<br> Temperature 150 °C
 4284 psi
<br>@Strain 2.90 %,<br> Temperature 302 °F
 ISO 11403-1 -2
34.29 MPa
<br>@Strain 4.13 %,<br> Temperature 150 °C
 4973 psi
<br>@Strain 4.13 %,<br> Temperature 302 °F
 ISO 11403-1 -2
37.28 MPa
<br>@Strain 2.01 %,<br> Temperature 90.0 °C
 5407 psi
<br>@Strain 2.01 %,<br> Temperature 194 °F
 ISO 11403-1 -2
41.59 MPa
<br>@Strain 8.81 %,<br> Temperature 150 °C
 6032 psi
<br>@Strain 8.81 %,<br> Temperature 302 °F
 ISO 11403-1 -2
42.9 MPa
<br>@Strain 1.14 %,<br> Temperature 40.0 °C
 6220 psi
<br>@Strain 1.14 %,<br> Temperature 104 °F
 ISO 11403-1 -2
46.08 MPa
<br>@Strain 2.98 %,<br> Temperature 90.0 °C
 6683 psi
<br>@Strain 2.98 %,<br> Temperature 194 °F
 ISO 11403-1 -2
55.57 MPa
<br>@Strain 1.06 %,<br> Temperature 23.0 °C
 8060 psi
<br>@Strain 1.06 %,<br> Temperature 73.4 °F
 ISO 11403-1 -2
57.4 MPa
<br>@Strain 1.72 %,<br> Temperature 40.0 °C
 8330 psi
<br>@Strain 1.72 %,<br> Temperature 104 °F
 ISO 11403-1 -2
64.13 MPa
<br>@Strain 1.17 %,<br> Temperature 0.000 °C
 9301 psi
<br>@Strain 1.17 %,<br> Temperature 32.0 °F
 ISO 11403-1 -2
69.5 MPa
<br>@Strain 2.41 %,<br> Temperature 40.0 °C
 10100 psi
<br>@Strain 2.41 %,<br> Temperature 104 °F
 ISO 11403-1 -2
72.53 MPa
<br>@Strain 1.48 %,<br> Temperature 23.0 °C
 10520 psi
<br>@Strain 1.48 %,<br> Temperature 73.4 °F
 ISO 11403-1 -2
73.93 MPa
<br>@Strain 1.26 %,<br> Temperature -40.0 °C
 10720 psi
<br>@Strain 1.26 %,<br> Temperature -40.0 °F
 ISO 11403-1 -2
81.35 MPa
<br>@Strain 1.54 %,<br> Temperature -20.0 °C
 11800 psi
<br>@Strain 1.54 %,<br> Temperature -4.00 °F
 ISO 11403-1 -2
83.86 MPa
<br>@Strain 1.61 %,<br> Temperature 0.000 °C
 12160 psi
<br>@Strain 1.61 %,<br> Temperature 32.0 °F
 ISO 11403-1 -2
88.48 MPa
<br>@Strain 2.02 %,<br> Temperature 23.0 °C
 12830 psi
<br>@Strain 2.02 %,<br> Temperature 73.4 °F
 ISO 11403-1 -2
100.33 MPa
<br>@Strain 2.09 %,<br> Temperature 0.000 °C
 14552 psi
<br>@Strain 2.09 %,<br> Temperature 32.0 °F
 ISO 11403-1 -2
102.47 MPa
<br>@Strain 2.03 %,<br> Temperature -20.0 °C
 14862 psi
<br>@Strain 2.03 %,<br> Temperature -4.00 °F
 ISO 11403-1 -2
108.32 MPa
<br>@Strain 1.89 %,<br> Temperature -40.0 °C
 15711 psi
<br>@Strain 1.89 %,<br> Temperature -40.0 °F
 ISO 11403-1 -2
114.02 MPa
<br>@Strain 2.69 %,<br> Temperature 0.000 °C
 16537 psi
<br>@Strain 2.69 %,<br> Temperature 32.0 °F
 ISO 11403-1 -2
120.82 MPa
<br>@Strain 2.59 %,<br> Temperature -20.0 °C
 17523 psi
<br>@Strain 2.59 %,<br> Temperature -4.00 °F
 ISO 11403-1 -2
135.83 MPa
<br>@Strain 3.28 %,<br> Temperature -20.0 °C
 19701 psi
<br>@Strain 3.28 %,<br> Temperature -4.00 °F
 ISO 11403-1 -2
136.63 MPa
<br>@Strain 2.53 %,<br> Temperature -40.0 °C
 19817 psi
<br>@Strain 2.53 %,<br> Temperature -40.0 °F
 ISO 11403-1 -2
10.0 MPa
<br>@Strain 0.210 %,<br> Time 360000 sec
 1450 psi
<br>@Strain 0.210 %,<br> Time 100 hour
 isochronous; ISO 11403-1 -2
10.0 MPa
<br>@Strain 0.240 %,<br> Time 3.60e+6 sec
 1450 psi
<br>@Strain 0.240 %,<br> Time 1000 hour
 isochronous; ISO 11403-1 -2
10.0 MPa
<br>@Strain 0.180 %,<br> Time 3600 sec
 1450 psi
<br>@Strain 0.180 %,<br> Time 1.00 hour
 isochronous; ISO 11403-1 -2
10.0 MPa
<br>@Strain 0.190 %,<br> Time 36000 sec
 1450 psi
<br>@Strain 0.190 %,<br> Time 10.0 hour
 isochronous; ISO 11403-1 -2
Elongation at Break 3.0 %
3.0 %
ISO 527-1/-2
Tensile Modulus 5.20 GPa
754 ksi
ISO 527-1/-2
1.484 GPa
<br>@Temperature 170 °C
 215.2 ksi
<br>@Temperature 338 °F
 Dynamic; ISO 11403-1 -2
1.917 GPa
<br>@Temperature 120 °C
 278.0 ksi
<br>@Temperature 248 °F
 ISO 11403-1 -2
1.985 GPa
<br>@Temperature 110 °C
 287.9 ksi
<br>@Temperature 230 °F
 Dynamic; ISO 11403-1 -2
3.807 GPa
<br>@Temperature 40.0 °C
 552.2 ksi
<br>@Temperature 104 °F
 ISO 11403-1 -2
5.113 GPa
<br>@Temperature 30.0 °C
 741.6 ksi
<br>@Temperature 86.0 °F
 Dynamic; ISO 11403-1 -2
5.524 GPa
<br>@Temperature -20.0 °C
 801.2 ksi
<br>@Temperature -4.00 °F
 Dynamic; ISO 11403-1 -2
5.899 GPa
<br>@Temperature -40.0 °C
 855.6 ksi
<br>@Temperature -40.0 °F
 ISO 11403-1 -2
6.295 GPa
<br>@Temperature -70.0 °C
 913.0 ksi
<br>@Temperature -94.0 °F
 Dynamic; ISO 11403-1 -2
6.753 GPa
<br>@Temperature -100 °C
 979.4 ksi
<br>@Temperature -148 °F
 Dynamic; ISO 11403-1 -2
Flexural Strength 150 MPa
21800 psi
ISO 178
Flexural Modulus 4.70 GPa
682 ksi
ISO 178
Shear Modulus 0.6414 GPa
<br>@Temperature 110 °C
 93.03 ksi
<br>@Temperature 230 °F
 Dynamic; ISO 11403-1 -2
0.8763 GPa
<br>@Temperature 70.0 °C
 127.1 ksi
<br>@Temperature 158 °F
 Dynamic; ISO 11403-1 -2
1.70 GPa
<br>@Temperature 20.0 °C
 247 ksi
<br>@Temperature 68.0 °F
 Dynamic; ISO 11403-1 -2
1.893 GPa
<br>@Temperature -40.0 °C
 274.5 ksi
<br>@Temperature -40.0 °F
 Dynamic; ISO 11403-1 -2
2.049 GPa
<br>@Temperature -70.0 °C
 297.2 ksi
<br>@Temperature -94.0 °F
 Dynamic; ISO 11403-1 -2
2.199 GPa
<br>@Temperature -100 °C
 318.9 ksi
<br>@Temperature -148 °F
 Dynamic; ISO 11403-1 -2
Users viewing this material also viewed the following: