SABIC Innovative Plastics LNP LUBRICOMP KI001XXJ Acetal
| Category | Polymer , Thermoplastic , Acetal (POM) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP KI001XXJ Acetal.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* LUBRICOMP* KI001XXJ is a compound based on Acetal containing 2% Silicone. Added features of this grade include: Wear Resistant, Healthcare.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.40 g/cc | 0.0506 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.240 % | 0.240 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.024 cm/cm @Time 86400 sec |
0.024 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.024 cm/cm @Time 86400 sec |
0.024 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 52.0 MPa | 7540 psi | Type I, 5 mm/min; ASTM D638 |
| Tensile Strength, Yield | 55.0 MPa | 7980 psi | Type I, 5 mm/min; ASTM D638 |
| Elongation at Break | 46 % | 46 % | Type I, 5 mm/min; ASTM D638 |
| Elongation at Yield | 16 % | 16 % | Type I, 5 mm/min; ASTM D638 |
| Tensile Modulus | 2.75 GPa | 399 ksi | 50 mm/min; ASTM D638 |
| Flexural Yield Strength | 74.0 MPa | 10700 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 2.28 GPa | 331 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Izod Impact, Notched | 0.810 J/cm | 1.52 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 15.5 J/cm | 29.0 ft-lb/in | ASTM D4812 |
| Coefficient of Friction, Dynamic | 0.44 | 0.44 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.34 | 0.34 | ASTM D3702 Modified |
| K (wear) Factor | 44.3 x 10-8 mm³/N-M | 22.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 106 °C @Thickness 3.20 mm |
223 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Polykemi AB POLYabs F20 UV4 ABS, UV-stabilized
- Nitriflex PDC-7423 NBR / PVC
- PolyOne Geon™ Vinyl Flexible R267AM Polyvinyl Chloride, Flexible (PVC, Flexible)
- DSM Akulon® K-FHGM35 (Dry) 40% Glass/Mineral Reinforced, Nylon 6 (North America) (discontinued **)
- LTL Color Compounds ColorFast® NY2GF131 Nylon 66, 13% Glass-Filled, Impact Modified
- Techmer ES Elastoblend® PA6/6 GF33 IM HS L 33% Glass Filled
- A. Schulman FORMION™ FI 341 Ionomer
- Trelleborg Emerson & Cuming Eccobond® 2780-45 One-Component High Temperature Performance Epoxy Adhesive
- Buckeye Polymers BP RPP 2009 GK (B) BLK Polypropylene, 20% Glass Filled
- Borealis LE6025 Polyethylene Modified Jacketing Compound
Copyright © lookpolymers.com All Rights Reserved