SABIC Innovative Plastics LNP LUBRICOMP LCL36E PEEK (Europe-Africa-Middle East)

Category	Polymer , Thermoplastic , Polyketone , Polyetheretherketone (PEEK)
Manufacturer	SABIC Innovative Plastics (GE Plastics)
Trade Name	LNP LUBRICOMP
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	SABIC Innovative Plastics LNP LUBRICOMP LCL36E PEEK (Europe-Africa-Middle East).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

LNP* LUBRICOMP* LCL36E is a compound based on Polyetheretherketone resin containing Carbon Fiber , PTFE. Added features include : Electrically Conductive, Internally Lubricated, Easy Molding.

Physical Properties	Metric	English	Comments
Density	1.50 g/cc	0.0542 lb/inÂ³	ISO 1183

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	224 MPa	32500 psi	5 mm/min; ISO 527
Elongation at Break	2.4 %	2.4 %	5 mm/min; ISO 527
Tensile Modulus	21.6 GPa	3130 ksi	1 mm/min; ISO 527
Flexural Strength	317 MPa	46000 psi	2 mm/min; ISO 178
Flexural Modulus	19.8 GPa	2870 ksi	2 mm/min; ISO 178
Izod Impact, Notched (ISO)	9.00 kJ/mÂ²	4.28 ft-lb/inÂ²	80104; ISO 180/1A
Izod Impact, Unnotched (ISO)	40.0 kJ/mÂ²	19.0 ft-lb/inÂ²	80104; ISO 180/1U

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	8.40 Âµm/m-Â°C @Temperature 23.0 - 60.0 Â°C	4.67 Âµin/in-Â°F @Temperature 73.4 - 140 Â°F	ISO 11359-2
CTE, linear, Transverse to Flow	42.0 Âµm/m-Â°C @Temperature 23.0 - 60.0 Â°C	23.3 Âµin/in-Â°F @Temperature 73.4 - 140 Â°F	ISO 11359-2
Deflection Temperature at 1.8 MPa (264 psi)	>= 300 Â°C	>= 572 Â°F	Flatw 80104 sp=64mm; ISO 75/Af

Electrical Properties	Metric	English	Comments
Surface Resistance	10 - 1000 ohm	10 - 1000 ohm	ASTM D257