SABIC Innovative Plastics LNP LUBRICOMP DX09410H PC
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP DX09410H PC.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* LUBRICOMP* DX09410H is a compound based on Polycarbonate resin containing Proprietary FIllers. Added features of this grade include: Healthcare, Wear Resistant.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.24 g/cc | 1.24 g/cc | ASTM D792 |
| Density | 1.23 g/cc | 0.0444 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.190 % | 0.190 % | 23°C / 50% RH; ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0080 - 0.010 cm/cm @Time 86400 sec |
0.0080 - 0.010 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0090 - 0.020 cm/cm @Time 86400 sec |
0.0090 - 0.020 in/in @Time 24.0 hour |
ASTM D955 |
| Melt Index of Compound | 5.0 g/10 min @Load 1.20 kg, Temperature 300 °C |
5.0 g/10 min @Load 2.65 lb, Temperature 572 °F |
MVR [cm^3/10 min]; ISO 1133 |
| 22 g/10 min @Load 2.16 kg, Temperature 330 °C |
22 g/10 min @Load 4.76 lb, Temperature 626 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 45.0 MPa | 6530 psi | 5 mm/min; ISO 527 |
| 51.0 MPa | 7400 psi | Type I, 5 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 62.0 MPa | 8990 psi | 5 mm/min; ISO 527 |
| 63.0 MPa | 9140 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 17.9 % | 17.9 % | 5 mm/min; ISO 527 |
| 45.7 % | 45.7 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 6.9 % | 6.9 % | Type I, 5 mm/min; ASTM D638 |
| 6.9 % | 6.9 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 2.20 GPa | 319 ksi | 1 mm/min; ISO 527 |
| 2.25 GPa | 326 ksi | 5 mm/min; ASTM D638 | |
| Flexural Strength | 78.0 MPa | 11300 psi | ISO 178 |
| 88.0 MPa | 12800 psi | ASTM D790 | |
| Flexural Modulus | 2.15 GPa | 312 ksi | 2 mm/min; ISO 178 |
| 2.29 GPa | 332 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 1.86 J/cm | 3.48 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 18.3 J/cm | 34.3 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 14.0 kJ/m² | 6.66 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 217 kJ/m² | 103 ft-lb/in² | 80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 73.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
40.6 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 74.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
41.1 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 132 °C | 270 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 138 °C @Thickness 3.20 mm |
280 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Osprey Metals 49FeCo2V Cobalt Alloy Powder (Grade 90% - 22)
- NanoAmor 95%, OD: 50-80 nm OH Functionalized Aligned Multi-Walled Carbon Nanotubes
- SABIC Innovative Plastics Lexan® EXL1810T PC Copolymer (Asia Pacific)
- Ravago Manufacturing Americas Hylon® N2000HL Nylon 6 (DAM)
- Kingfa FW-650 Flame Retardant ABS
- Karina 805-18/105-IS-SD Gray PVC Compound
- A. Schulman POLYBLAK™ 4669 Premium Conductive 35% Carbon Black Concentrate Based In LLDPE
- Dow Retain® 8209 ABS + Polycarbonate
- Chem Polymer Chemlon 217 GI Nylon 6, 17% Glass Fiber Reinforced
Copyright © lookpolymers.com All Rights Reserved