Hexcel® HexWeb® CR-PAA™ 1/4-5052-0.002 Phosphoric Acid Anodized Aluminum Honeycomb

Category Metal , Metal Foam, Mesh, or Honeycomb , Nonferrous Metal , Aluminum Alloy , 5000 Series Aluminum Alloy
Manufacturer Hexcel
Trade Name HexWeb®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Hexcel® HexWeb® CR-PAA™ 1/4-5052-0.002 Phosphoric Acid Anodized Aluminum Honeycomb.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Grade is designated as "Cell Size-Alloy-Foil Gauge." The life cycle of aluminum honeycomb sandwich structures in a given application can be directly related to the quality of the bond between the face sheets that carry bending loads and the honeycomb that carries the shear loads. The adhesive is the interface between the facing and the core in the same way that the oxide on the aluminum and the primer that has been applied to it is the interface between the honeycomb substrate material and the bonding adhesive. This interface is critical to the performance of honeycomb bonded assemblies.HexWeb® CR-PAA™ is designed for aircraft structures that are exposed to demanding environmental conditions. HexWeb® CR-PAA™ outperforms standard MIL-C-7438 core in salt spray and HexWeb® crack propagation tests.
Physical Properties Metric English Comments
Density 0.0689 g/cc
0.00249 lb/in³
Nominal
Mechanical Properties Metric English Comments
Compressive Yield Strength >= 2.41 MPa
>= 350 psi
Bare, min
>= 2.55 MPa
>= 370 psi
Stabilized, min
3.45 MPa
500 psi
Bare, typ
3.72 MPa
540 psi
Stabilized, typ
Compressive Modulus 0.965 GPa
140 ksi
Stabilized, typ
Shear Modulus 0.205 GPa
29.8 ksi
Plate Shear, W Direction, typ
0.455 GPa
66.0 ksi
Plate Shear, L Direction, typ
Shear Strength >= 1.07 MPa
>= 155 psi
Plate Shear, W Direction, min
1.38 MPa
200 psi
Plate Shear, W Direction, typ
>= 1.83 MPa
>= 265 psi
Plate Shear, L Direction, min
2.21 MPa
320 psi
Plate Shear, L Direction, typ