A. Schulman FORMION™ FI 388 Ionomer
| Category | Polymer , Thermoplastic , Ionomer |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | A. Schulman FORMION™ FI 388 Ionomer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by A. Schulman.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.27 g/cc | 1.27 g/cc | ISO 1183/1 |
| Linear Mold Shrinkage | 0.0010 - 0.0030 cm/cm @Thickness 3.20 mm |
0.0010 - 0.0030 in/in @Thickness 0.126 in |
72 hr; ISO 294 |
| 0.0020 - 0.0050 cm/cm @Thickness 3.20 mm |
0.0020 - 0.0050 in/in @Thickness 0.126 in |
aged 48 hrs at 121°C; ISO 294 | |
| Melt Index of Compound | 1.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
1.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
Cond. E; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 62 | 62 | 15 sec delay; ISO 868 |
| Tensile Strength, Ultimate | 38.0 MPa | 5510 psi | at max load; ISO 527 |
| Elongation at Break | 5.0 % | 5.0 % | ISO 527 |
| Flexural Modulus | 3.45 GPa | 500 ksi | Tangent; ISO 178 |
| Izod Impact, Notched (ISO) | 16.0 kJ/m² | 7.61 ft-lb/in² | ISO 180 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 88.0 °C @Thickness 3.20 mm |
190 °F @Thickness 0.126 in |
ISO 75 |
Users viewing this material also viewed the following:
- PolyOne OnForce™ LFT NN-50LGF/000 HS UV Black Polyamide 66 (Nylon 66)
- North Wood Plastics 60 HDPE + UNIFILL (40% Wood Fiber)
- DuPont™ Sclairfilm® GL-1 LLDPE Film, Laminating, 38.1 µm Thickness (discontinued **)
- LG Chemical LI-913 ASA, Injection Molding, High Impact
- Industeel SIRIUS 310 25% Cr - 0.6% Si Heat Resistant Stainless Steel
- Lanxess Durethan® DP BM 410 H2.0 901510 Nylon 6, 10% Mineral + Glass Fiber
- A. Schulman POLYBATCH™ Blue 40460/4 Concentrate Based In LLDPE
- ChevronTexaco Capella® WF 68
- Cadi 3WC Tungsten Copper
- Alliance Polymers Viprene™ P55A-22U-NAT Thermoplastic Vulcanizate Elastomer
Copyright © lookpolymers.com All Rights Reserved