SABIC Innovative Plastics GELOY XP4025 ASA (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , ASA Polymer |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | GELOY |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics GELOY XP4025 ASA (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
GELOY XP4025 is a high heat modified ASA/PC blend, for automotive exterior applications. It shows very good properties, gloss and colour retention, as well as faster cycle time over competitive material.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.15 g/cc | 0.0415 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.250 % | 0.250 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.70 % | 0.70 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0060 cm/cm | 0.0040 - 0.0060 in/in | on Tensile Bar; SABIC Method |
| Melt Index of Compound | 5.0 g/10 min @Load 10.0 kg, Temperature 220 °C |
5.0 g/10 min @Load 22.0 lb, Temperature 428 °F |
MVR [cm^3/10 min]; ISO 1133 |
| 18 g/10 min @Load 5.00 kg, Temperature 260 °C |
18 g/10 min @Load 11.0 lb, Temperature 500 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 115 | 115 | ISO 2039-2 |
| Hardness, H358/30 | 98.0 MPa | 14200 psi | ISO 2039-1 |
| Tensile Strength at Break | 40.0 MPa | 5800 psi | 5 mm/min; ISO 527 |
| 45.0 MPa | 6530 psi | 50 mm/min; ISO 527 | |
| Tensile Strength, Yield | 50.0 MPa | 7250 psi | 5 mm/min; ISO 527 |
| 55.0 MPa | 7980 psi | 50 mm/min; ISO 527 | |
| Elongation at Break | 15 % | 15 % | 5 mm/min; ISO 527 |
| 15 % | 15 % | 50 mm/min; ISO 527 | |
| Elongation at Yield | 4.0 % | 4.0 % | 5 mm/min; ISO 527 |
| 4.0 % | 4.0 % | 50 mm/min; ISO 527 | |
| Tensile Modulus | 2.30 GPa | 334 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 80.0 MPa | 11600 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 2.35 GPa | 341 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 15.0 kJ/m² | 7.14 ft-lb/in² | 80*10*4; ISO 180/1A |
| 6.00 kJ/m² @Temperature -30.0 °C |
2.86 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| 6.00 kJ/m² @Temperature -40.0 °C |
2.86 ft-lb/in² @Temperature -40.0 °F |
80*10*4; ISO 180/1A | |
| 8.00 kJ/m² @Temperature -10.0 °C |
3.81 ft-lb/in² @Temperature 14.0 °F |
80*10*4; ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | NB | NB | 80*10*4; ISO 180/1U |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
80*10*4; ISO 180/1U | |
| Charpy Impact Unnotched | NB | NB | Edgew 80*10*4 sp=62mm; ISO 179/1eU |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
Edgew 80*10*4 sp=62mm; ISO 179/1eU | |
| Charpy Impact, Notched | 1.40 J/cm² | 6.66 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| 0.700 J/cm² @Temperature -30.0 °C |
3.33 ft-lb/in² @Temperature -22.0 °F |
Edgew 80*10*4 sp=62mm; ISO 179/1eA | |
| Taber Abrasion, mg/1000 Cycles | 140 | 140 | CS-17, 1 kg; SABIC Method |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 70.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
38.9 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 90.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
50.0 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Thermal Conductivity | 0.240 W/m-K | 1.67 BTU-in/hr-ft²-°F | ISO 8302 |
| Deflection Temperature at 0.46 MPa (66 psi) | 104 °C | 219 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
| Deflection Temperature at 1.8 MPa (264 psi) | 86.0 °C | 187 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| Vicat Softening Point | 104 °C | 219 °F | Rate B/50; ISO 306 |
| 107 °C | 225 °F | Rate B/120; ISO 306 | |
| UL RTI, Electrical | 50.0 °C | 122 °F | UL 746B |
| UL RTI, Mechanical with Impact | 50.0 °C | 122 °F | UL 746B |
| UL RTI, Mechanical without Impact | 50.0 °C | 122 °F | UL 746B |
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
UL 94 |
| HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
UL 94 | |
| Oxygen Index | 20 % | 20 % | ISO 4589 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | >= 1.00e+16 ohm | >= 1.00e+16 ohm | ROA; IEC 60093 |
| Dielectric Constant | 3.0 @Frequency 1.00e+6 Hz |
3.0 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 4.3 @Frequency 50.0 - 60.0 Hz |
4.3 @Frequency 50.0 - 60.0 Hz |
IEC 60250 | |
| Dielectric Strength | 27.0 kV/mm @Thickness 3.20 mm |
686 kV/in @Thickness 0.126 in |
in oil; IEC 60243-1 |
| Dissipation Factor | 0.021 @Frequency 1.00e+6 Hz |
0.021 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 0.18 @Frequency 50.0 - 60.0 Hz |
0.18 @Frequency 50.0 - 60.0 Hz |
IEC 60250 | |
| Comparative Tracking Index | 225 V | 225 V | IEC 60112 |
| >= 225 V | >= 225 V | IEC 60112 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Ball Pressure Test, 75°C +/- 2°C | PASSES | IEC 60695-10-2 |
Users viewing this material also viewed the following:
- Quadrant EPP Monocast® MC 904P Nylon for Pile Driver Pads (ASTM Product Data Sheet)
- Lucky CG-920 Acrylic
- Techmer ES HiFill® PA6/6 GB25 L BK 25% Glass Bead Filler
- SABIC Innovative Plastics Noryl ENV85 PPE+PS (Asia Pacific)
- A. Schulman POLYFORT™ FXP 3000-3120 Glass Sphere Filled Copolymer Polypropylene
- Zeon Chemicals Zetpol® 2030L Hydrogenated Nitrile Elastomomer
- 3M FM0139 Indoor UL Recognized Clear Polyester Overlaminate Label Product
- Asia International Enterprise (Hong Kong) 60T4 Nylon 66, 20% Filled
- Bhansali Engineering Santron IMS 2007LF SAN Resin
Copyright © lookpolymers.com All Rights Reserved