SABIC Innovative Plastics Cycoloy® C6850REC PC+ABS (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Cycoloy® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Cycoloy® C6850REC PC+ABS (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PC+ABS Industrial quality. Flame retardant. Limited colors only (Black and Grey)This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.19 g/cc | 0.0430 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 0.070 % | 0.070 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.29 % @Temperature 23.0 °C |
0.29 % @Temperature 73.4 °F |
ISO 62 |
| Melt Flow | 12 g/10 min @Load 2.16 kg, Temperature 260 °C |
12 g/10 min @Load 4.76 lb, Temperature 500 °F |
[cm^3/10 min] Melt Volume Rate; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 51.0 MPa | 7400 psi | 50 mm/min; ISO 527 |
| Tensile Strength, Yield | 65.0 MPa | 9430 psi | 50 mm/min; ISO 527 |
| Elongation at Break | 50 % | 50 % | 50 mm/min; ISO 527 |
| Elongation at Yield | 4.5 % | 4.5 % | 50 mm/min; ISO 527 |
| Tensile Modulus | 2.90 GPa | 421 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 98.0 MPa | 14200 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 2.60 GPa | 377 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 7.00 kJ/m² @Temperature -30.0 °C |
3.33 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A |
| 10.0 kJ/m² @Temperature -30.0 °C |
4.76 ft-lb/in² @Temperature -22.0 °F |
80*10*3; ISO 180/1A | |
| 15.0 kJ/m² @Temperature 23.0 °C |
7.14 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A | |
| 15.0 kJ/m² @Temperature 23.0 °C |
7.14 ft-lb/in² @Temperature 73.4 °F |
80*10*3; ISO 180/1A | |
| Charpy Impact, Notched | 1.00 J/cm² @Temperature -30.0 °C |
4.76 ft-lb/in² @Temperature -22.0 °F |
V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| 1.00 J/cm² @Temperature -30.0 °C |
4.76 ft-lb/in² @Temperature -22.0 °F |
V-notch Edgew 80*10*3 sp=62mm; ISO 179/1eA | |
| 1.50 J/cm² @Temperature 23.0 °C |
7.14 ft-lb/in² @Temperature 73.4 °F |
V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA | |
| 1.50 J/cm² @Temperature 23.0 °C |
7.14 ft-lb/in² @Temperature 73.4 °F |
V-notch Edgew 80*10*3 sp=62mm; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 67.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
37.2 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 69.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
38.3 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 98.0 °C | 208 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
| Deflection Temperature at 1.8 MPa (264 psi) | 89.0 °C | 192 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| Vicat Softening Point | 107 °C | 225 °F | Rate B/50; ISO 306 |
| 110 °C | 230 °F | Rate B/120; ISO 306 | |
| UL RTI, Electrical | 80.0 °C | 176 °F | UL 746B |
| UL RTI, Mechanical with Impact | 70.0 °C | 158 °F | UL 746B |
| UL RTI, Mechanical without Impact | 80.0 °C | 176 °F | UL 746B |
| Flammability, UL94 | V-1 @Thickness 1.50 mm |
V-1 @Thickness 0.0591 in |
UL 94 by SABIC-IP |
| V-0 @Thickness 2.30 mm |
V-0 @Thickness 0.0906 in |
UL 94 by SABIC-IP | |
| 5VB @Thickness 2.30 mm |
5VB @Thickness 0.0906 in |
UL 94 by SABIC-IP |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 4.50e+16 ohm-cm | 4.50e+16 ohm-cm | IEC 60093 |
| Surface Resistance | 5.00e+16 ohm | 5.00e+16 ohm | ROA; IEC 60093 |
| Dielectric Constant | 2.8 @Frequency 1.00e+6 Hz |
2.8 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 2.8 @Frequency 50.0 - 60.0 Hz |
2.8 @Frequency 50.0 - 60.0 Hz |
IEC 60250 | |
| Dielectric Strength | 30.0 kV/mm @Thickness 1.60 mm |
762 kV/in @Thickness 0.0630 in |
in oil; IEC 60243-1 |
| Dissipation Factor | 0.0060 @Frequency 1.00e+6 Hz |
0.0060 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 0.011 @Frequency 50.0 - 60.0 Hz |
0.011 @Frequency 50.0 - 60.0 Hz |
IEC 60250 | |
| Comparative Tracking Index | 275 V | 275 V | IEC 60112 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Ball Pressure Test, 75°C +/- 2°C | passes | IEC 60695-10-2 |
Users viewing this material also viewed the following:
- Fiberfil® M-2450 Polypropylene Copolymer
- SYNTHOS Kralex® 1739 Styrene Butadiene Rubber
- Solvay Specialty Polymers Catalyst CT/2-LR Polyolefin
- SSAB Tunnplat Domex® 700MC HSLA Steel
- SABIC Innovative Plastics Valox® 430 PBT
- Sumitomo Chemical ESPOLEX® WT525 Thermoplastic Elastomer
- Formosa Plastics Formolon® 28 PVC
- A. Schulman POLYBATCH™ Yellow 26787V Concentrate Based In LDPE
- Covestro Bayflex® 180 Polyurethane Elastomeric RIM, 20% Mineral Filled, MDI-based 2-Component Liquid System
- Axiall 18760 Wire & Cable Flexible PVC
Copyright © lookpolymers.com All Rights Reserved