- Acrylonitrile Butadiene Styrene (ABS), Heat Resistant, Molded
- SABIC Innovative Plastics Cycolac® X15 ABS
SABIC Innovative Plastics Cycolac® X15 ABS
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Heat Resistant, Molded |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Cycolac® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Cycolac® X15 ABS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Automotive. Very high heat resistance with high impact. UL94 HB rated. High gloss.This data was supplied by SABIC-IP for the Americas region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.05 g/cc | 1.05 g/cc | ASTM D 792 |
| Viscosity | 255000 cP @Temperature 260 °C |
255000 cP @Temperature 500 °F |
melt; 1000 sec-1; ASTM D 3825 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0080 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0080 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 1.0 g/10 min @Load 3.80 kg, Temperature 230 °C |
1.0 g/10 min @Load 8.38 lb, Temperature 446 °F |
ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 108 | 108 | ASTM D 785 |
| Tensile Strength, Yield | 45.0 MPa | 6530 psi | Type I, 5 mm/min; ASTM D 638 |
| Tensile Modulus | 2.20 GPa | 319 ksi | 5 mm/min; ASTM D 638 |
| Flexural Yield Strength | 77.0 MPa | 11200 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| Flexural Modulus | 2.34 GPa | 339 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| Izod Impact, Notched | 0.850 J/cm @Temperature -40.0 °C |
1.59 ft-lb/in @Temperature -40.0 °F |
ASTM D 256 |
| 2.67 J/cm @Temperature 23.0 °C |
5.00 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 107 °C @Thickness 3.20 mm |
225 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| 110 °C @Thickness 6.40 mm |
230 °F @Thickness 0.252 in |
unannealed; ASTM D 648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 94.0 °C @Thickness 3.20 mm |
201 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| 100 °C @Thickness 6.40 mm |
212 °F @Thickness 0.252 in |
unannealed; ASTM D 648 | |
| UL RTI, Electrical | 60.0 °C | 140 °F | UL 746B |
| UL RTI, Mechanical with Impact | 60.0 °C | 140 °F | UL 746B |
| UL RTI, Mechanical without Impact | 60.0 °C | 140 °F | UL 746B |
| Flammability, UL94 | HB @Thickness 1.47 mm |
HB @Thickness 0.0579 in |
UL 94 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Arc Resistance | 60 - 120 sec | 60 - 120 sec | Tungsten, PLC code 6; ASTM D 495 |
| Comparative Tracking Index | >= 600 V | >= 600 V | PLC code 0; UL 746A |
| Hot Wire Ignition, HWI | 7.0 - 15 sec | 7.0 - 15 sec | PLC code 4; UL 746A |
| High Amp Arc Ignition, HAI | >= 120 arcs | >= 120 arcs | surface, PLC code 0; UL 746A |
| High Voltage Arc-Tracking Rate, HVTR | 25.4 - 80.0 mm/min | 1.00 - 3.15 in/min | PLC code 2; UL 746A |
Users viewing this material also viewed the following:
- Polykemi AB POLYfill PPHC GF3020 PB7 Polypropylene, Glass Fibre-Reinforced, Chemically Coupled
- Kinlead HSS11 Normal Grade Heat Sealable Film (thickness: 25 µm)
- Lehmann & Voss LUVOCOM® 1106-8133 Polyether imide, with carbon fiber, easy flowing
- LG Chemical LUPOL HR2100D PP+GF17%
- SABIC Innovative Plastics Xenoy® XLG2400 PC+PET
- Samsung Cheil Industries Infino® VB-5305G PBT, Glass Filled FR
- SK Chemicals SKYTHANE® U9081E Hardener
- Trimay® Wear Plate T157 Iron-based Steel Overlay
- DuPont Performance Polymers Hytrel® 4056P Polyester Elastomer TPC-ET (Unverified Data**)