SABIC Innovative Plastics LNP THERMOCOMP DE004ERP PC
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP DE004ERP PC.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Thermocomp* DE004ERP is a compound based on Polycarbonate resin containing 20% Carbon Fiber. Added features include: Electrically Conductive, Easy Molding, Mold Release.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.26 g/cc | 0.0455 lb/in³ | ISO 1183 |
| 1.27 g/cc | 0.0459 lb/in³ | ASTM D792 | |
| Moisture Absorption | 0.100 % | 0.100 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0019 cm/cm @Time 86400 sec |
0.0019 in/in @Time 24.0 hour |
ISO 294 |
| 0.0010 - 0.0030 cm/cm @Time 86400 sec |
0.0010 - 0.0030 in/in @Time 24.0 hour |
ASTM D955 | |
| Linear Mold Shrinkage, Transverse | 0.0059 cm/cm @Time 86400 sec |
0.0059 in/in @Time 24.0 hour |
ISO 294 |
| 0.0050 - 0.0070 cm/cm @Time 86400 sec |
0.0050 - 0.0070 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 116 MPa | 16800 psi | ASTM D638 |
| 116 MPa | 16800 psi | ISO 527 | |
| Tensile Strength, Yield | 116 MPa | 16800 psi | ASTM D638 |
| 116 MPa | 16800 psi | ISO 527 | |
| Elongation at Break | 1.9 % | 1.9 % | ASTM D638 |
| 2.0 % | 2.0 % | ISO 527 | |
| Elongation at Yield | 1.9 % | 1.9 % | ASTM D638 |
| 2.0 % | 2.0 % | ISO 527 | |
| Tensile Modulus | 11.1 GPa | 1610 ksi | 1 mm/min; ISO 527 |
| 11.72 GPa | 1700 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 151 MPa | 21900 psi | ASTM D790 |
| 172 MPa | 24900 psi | ISO 178 | |
| Flexural Modulus | 8.96 GPa | 1300 ksi | ASTM D790 |
| 9.70 GPa | 1410 ksi | ISO 178 | |
| Izod Impact, Notched | 0.740 J/cm | 1.39 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 4.53 J/cm | 8.49 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 7.00 kJ/m² | 3.33 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 28.0 kJ/m² | 13.3 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 14.0 J | 10.3 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 3.00 J | 2.21 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 61.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
33.9 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 61.2 µm/m-°C @Temperature -40.0 - 40.0 °C |
34.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| CTE, linear, Transverse to Flow | 10.8 µm/m-°C @Temperature -40.0 - 40.0 °C |
6.00 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 11.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
6.11 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 148 °C | 298 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 147 °C @Thickness 3.20 mm |
297 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 144 °C | 291 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 143 °C @Thickness 3.20 mm |
289 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Menzolit Menzolit® SMC 0400 Unsaturated Polyester UP
- Industeel SUPRALSIM® 690 HLE Steel for Welded and Weight-Saving Structures
- Karina 800D48/1-A-IS-BZ Black PVC Compound
- Wellman Wellamid® GF33-66 22LH-N 33% Glass Fiber Reinforced Nylon 66, Lubricated & Heat Stabilized
- A. Schulman POLYBATCH™ Navajo 10294U/4 Concentrate Based In LLDPE
- Aclo Accutech Polypropylene Copolymer CP0436M10L Mica Reinforced
- Arlon 55272R024 0.024" (0.610 mm) Cured Silicone Rubber with Fiberglass Substrate
- Bulk Molding Compounds BMC T10(14) General Purpose Molding Compound
- BASF Ultradur® S 4090 G6X 30% Glass Filled PBT
Copyright © lookpolymers.com All Rights Reserved