SABIC Innovative Plastics Cycolac® MG38U ABS
| Category | Polymer , Thermoplastic , ABS Polymer |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Cycolac® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Cycolac® MG38U ABS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
High impact ABS. UL 746C f1 listed. Toughness/rigidity. Good fatigue resistance.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.05 g/cc | 1.05 g/cc | ASTM D792 |
| Density | 1.05 g/cc | 0.0379 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.200 % | 0.200 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 1.0 % | 1.0 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0080 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0080 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 15 g/10 min @Load 10.0 kg, Temperature 220 °C |
15 g/10 min @Load 22.0 lb, Temperature 428 °F |
ISO 1133 |
| Melt Index of Compound | 5.0 g/10 min @Load 5.00 kg, Temperature 220 °C |
5.0 g/10 min @Load 11.0 lb, Temperature 428 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 33.0 MPa | 4790 psi | 5 mm/min; ISO 527 |
| 36.0 MPa | 5220 psi | Type I, 5 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 41.0 MPa | 5950 psi | 5 mm/min; ISO 527 |
| 43.0 MPa | 6240 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 30 % | 30 % | 5 mm/min; ISO 527 |
| 98 % | 98 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 2.5 % | 2.5 % | 5 mm/min; ISO 527 |
| 2.9 % | 2.9 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 2.39 GPa | 347 ksi | 5 mm/min; ASTM D638 |
| 2.41 GPa | 350 ksi | 1 mm/min; ISO 527 | |
| Flexural Yield Strength | 70.0 MPa | 10200 psi | 2 mm/min; ISO 178 |
| 76.0 MPa | 11000 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 2.31 GPa | 335 ksi | 2 mm/min; ISO 178 |
| 2.41 GPa | 350 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 3.74 J/cm | 7.01 ft-lb/in | ASTM D256 |
| Izod Impact, Notched (ISO) | 27.0 kJ/m² | 12.8 ft-lb/in² | 80*10*4; ISO 180/1A |
| Dart Drop, Total Energy | 32.0 J @Temperature 23.0 °C |
23.6 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 88.2 µm/m-°C @Temperature -40.0 - 40.0 °C |
49.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 88.2 µm/m-°C @Temperature -40.0 - 40.0 °C |
49.0 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 86.4 µm/m-°C @Temperature -40.0 - 40.0 °C |
48.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 86.4 µm/m-°C @Temperature -40.0 - 40.0 °C |
48.0 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 97.0 °C @Thickness 3.20 mm |
207 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 80.0 °C | 176 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 82.0 °C @Thickness 3.20 mm |
180 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 98.0 °C | 208 °F | Rate B/50; ASTM D1525 |
| 98.0 °C | 208 °F | Rate B/50; ISO 306 | |
| 99.0 °C | 210 °F | Rate B/120; ISO 306 | |
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
UL 94 |
Users viewing this material also viewed the following:
- Polimeri Europa Clearflex® FG 336 Hexene Copolymer Linear Low Density Polyethylene
- Quadrant EPP TIVAR® SuperPlus PE-UHMW + specific additives (ISO Data)
- Parker Chomerics CHO-SEAL® 6307 Conductive Elastomer
- GEHR Plastics POM-10PE Acetal Copolymer
- Solvay Specialty Polymers Diofan® A 586 Polyvinylidene Chloride (PVDC)
- Borealis SuperCOPO™ LE4205R Polyethylene Insulation Compound, Crosslinkable
- Westlake Plastics Tefzel® 2181 ETFE
- Chevron Phillips Marlex® HXB TR-512 Extra high molecular weight polyethylene
- Akzo Nobel Trigonox® SBPS Polymerization Initiator
Copyright © lookpolymers.com All Rights Reserved