SABIC Innovative Plastics Cycolac® FR30U ABS

Category Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Unreinforced, Flame Retardant
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Cycolac®
Port Ningbo port,China
Trade Terms EXW, FOB, CFR, CIF
Payment Terms L/C, T/T, PayPal
Download PDF SABIC Innovative Plastics Cycolac® FR30U ABS.pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
Flame retardant ABS. Good indoor UV properties. Excellent moldability with no bloom. V-1/V-0/5VB rated.This data was supplied by SABIC-IP for the Americas region.
Physical Properties Metric English Comments
Specific Gravity 1.17 g/cc
1.17 g/cc
ASTM D 792
Viscosity 350000 cP
<br>@Temperature 200 °C
 350000 cP
<br>@Temperature 392 °F
 melt; 1000 sec-1; ASTM D 3825
Linear Mold Shrinkage, Flow 0.0050 - 0.0080 cm/cm
<br>@Thickness 3.20 mm
 0.0050 - 0.0080 in/in
<br>@Thickness 0.126 in
 SABIC Method
Melt Flow 5.3 g/10 min
<br>@Load 3.80 kg,<br> Temperature 230 °C
 5.3 g/10 min
<br>@Load 8.38 lb,<br> Temperature 446 °F
 ASTM D 1238
7.0 g/10 min
<br>@Load 5.00 kg,<br> Temperature 220 °C
 7.0 g/10 min
<br>@Load 11.0 lb,<br> Temperature 428 °F
 ISO 1133
28 g/10 min
<br>@Load 10.0 kg,<br> Temperature 220 °C
 28 g/10 min
<br>@Load 22.0 lb,<br> Temperature 428 °F
 [cm^3/10 min] Melt Volume Rate; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 33.0 MPa
4790 psi
Type I, 5 mm/min; ASTM D 638
Tensile Strength, Yield 39.0 MPa
5660 psi
Type I, 5 mm/min; ASTM D 638
Elongation at Break 10 %
10 %
Type I, 5 mm/min; ASTM D 638
Elongation at Yield 2.3 %
2.3 %
Type I, 5 mm/min; ASTM D 638
Tensile Modulus 2.20 GPa
319 ksi
5 mm/min; ASTM D 638
Flexural Yield Strength 68.0 MPa
9860 psi
1.3 mm/min, 50 mm span; ASTM D 790
Flexural Modulus 2.42 GPa
351 ksi
1.3 mm/min, 50 mm span; ASTM D 790
Izod Impact, Notched 3.20 J/cm
<br>@Temperature 23.0 °C
 5.99 ft-lb/in
<br>@Temperature 73.4 °F
 ASTM D 256
Impact Test 39.0 J
<br>@Temperature 23.0 °C
 28.8 ft-lb
<br>@Temperature 73.4 °F
 Instrumented Impact Total Energy; ASTM D 3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 84.6 µm/m-°C
<br>@Temperature -40.0 - 40.0 °C
 47.0 µin/in-°F
<br>@Temperature -40.0 - 104 °F
 ASTM E 831
CTE, linear, Transverse to Flow 88.2 µm/m-°C
<br>@Temperature -40.0 - 40.0 °C
 49.0 µin/in-°F
<br>@Temperature -40.0 - 104 °F
 ASTM E 831
Deflection Temperature at 0.46 MPa (66 psi) 88.0 °C
<br>@Thickness 3.20 mm
 190 °F
<br>@Thickness 0.126 in
 unannealed; ASTM D 648
Deflection Temperature at 1.8 MPa (264 psi) 75.0 °C
<br>@Thickness 3.20 mm
 167 °F
<br>@Thickness 0.126 in
 unannealed; ASTM D 648
Vicat Softening Point 94.0 °C
201 °F
Rate B/50; ASTM D 1525
UL RTI, Electrical 60.0 °C
140 °F
UL 746B
UL RTI, Mechanical with Impact 60.0 °C
140 °F
UL 746B
UL RTI, Mechanical without Impact 60.0 °C
140 °F
UL 746B
Flammability, UL94 V-1
<br>@Thickness 2.31 mm
 V-1
<br>@Thickness 0.0909 in
 UL 94
V-0
<br>@Thickness 2.99 mm
 V-0
<br>@Thickness 0.118 in
 UL 94
5VB
<br>@Thickness 2.31 mm
 5VB
<br>@Thickness 0.0909 in
 UL 94