SABIC Innovative Plastics Cycolac® BDT5510 ABS
| Category | Polymer , Thermoplastic , ABS Polymer |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Cycolac® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Cycolac® BDT5510 ABS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Automotive. High heat resistance, low gloss, color concentratable for interior applications. Natural only.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.05 g/cc | 1.05 g/cc | ASTM D792 |
| Viscosity | 163000 cP | 163000 cP | Melt Viscosity, 260°C, 1000 sec-1; ASTM D3825 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0080 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0080 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 6.0 g/10 min @Load 3.80 kg, Temperature 230 °C |
6.0 g/10 min @Load 8.38 lb, Temperature 446 °F |
ASTM D1238 |
| 14 g/10 min @Load 10.0 kg, Temperature 220 °C |
14 g/10 min @Load 22.0 lb, Temperature 428 °F |
ISO 1133 | |
| Spiral Flow | 73.66 cm @Temperature 260 °C |
29.00 in @Temperature 500 °F |
10 ips,3.175 X 1524 mm |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 43.0 MPa | 6240 psi | 50 mm/min; ISO 527 |
| 53.0 MPa | 7690 psi | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 2.27 GPa | 329 ksi | 5 mm/min; ASTM D638 |
| 2.93 GPa | 425 ksi | 1 mm/min; ISO 527 | |
| Flexural Yield Strength | 67.0 MPa | 9720 psi | 2 mm/min; ISO 178 |
| 81.0 MPa | 11700 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 2.03 GPa | 294 ksi | 2 mm/min; ISO 178 |
| 2.46 GPa | 357 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 2.93 J/cm | 5.49 ft-lb/in | ASTM D256 |
| Izod Impact, Notched (ISO) | 12.0 kJ/m² | 5.71 ft-lb/in² | 80*10*4; ISO 180/1A |
| 7.00 kJ/m² @Temperature -30.0 °C |
3.33 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| Charpy Impact, Notched | 1.30 J/cm² | 6.19 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| 0.700 J/cm² @Temperature -30.0 °C |
3.33 ft-lb/in² @Temperature -22.0 °F |
Edgew 80*10*4 sp=62mm; ISO 179/1eA | |
| Dart Drop, Total Energy | 35.0 J | 25.8 ft-lb | ASTM D3029 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 135 µm/m-°C @Temperature -40.0 - 60.0 °C |
75.0 µin/in-°F @Temperature -40.0 - 140 °F |
ASTM E 831 |
| Deflection Temperature at 0.46 MPa (66 psi) | 95.0 °C | 203 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 92.0 °C @Thickness 3.20 mm |
198 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 83.0 °C | 181 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 81.0 °C @Thickness 3.20 mm |
178 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 98.0 °C | 208 °F | Rate B/50; ISO 306 |
| Flammability, UL94 | HB @Thickness 1.52 mm |
HB @Thickness 0.0598 in |
UL 94 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Gloss | 25 % | 25 % | untextured, 60 degrees; ASTM D523 |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Packaging XPL189 Amber 1505 Polyvinyl Chloride, Rigid (PVC, Rigid)
- Materion Beryllium Copper Alloy 25 Tube; H (TD04) Temper; 0ver 25.4 to 76 mm o.d. (UNS C17200)
- Loxim 220 12V0 Polybutylene Terephthalate
- SABIC Innovative Plastics LNP THERMOCOMP TH0300B PU
- Elastomer Engineering E50D Polyurethane
- Eurostar Starpylen HU 30BF4 PP, 30% Bamboo Fiber Filled, Injection Molding
- Colorite Polymers 8077 Non-Phthalate 77 Series Vinyl Compound
- ExxonMobil Escorene® LD 783.ND Molding, extrusion and compounding resin (discontinued **)
- Indium Corp. Indalloy 214 Silver Solder Alloy
- Adamas Adalon® 254 PTFE, 28% Glass Fiber
Copyright © lookpolymers.com All Rights Reserved