SABIC FI0750 Bimodal High Density Polyethylene for Blown Film

Category	Polymer , Film , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Film Grade
Manufacturer	SABIC
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	SABIC FI0750 Bimodal High Density Polyethylene for Blown Film.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Product Description: FI0750 is a high molecular weight high density polyethylene copolymer grade specifically designed for blown film applications. Its high molecular weight, broad molecular weight distribution and high density combine successfully to give excellent extrudability with high film strength and rigidity.Typical Applications: FI0750 is recommended for blown film extrusion. It can be used for producing grocery sacks, shopping bags, refuse bags, thin films for bag on roll, wrapping film and also for replacement of thin paper products. Films produced with this product can be readily treated and printed to give high quality graphics.Information provided by SABIC.

Physical Properties	Metric	English	Comments
Density	0.950 g/cc	0.0343 lb/in³	ISO 1183
Thickness	20.0 microns	0.787 mil
Melt Flow	0.22 g/10 min @Load 5.00 kg, Temperature 190 °C	0.22 g/10 min @Load 11.0 lb, Temperature 374 °F	ISO 1133
	7.5 g/10 min @Load 21.6 kg, Temperature 190 °C	7.5 g/10 min @Load 47.6 lb, Temperature 374 °F	ISO 1133

Mechanical Properties	Metric	English	Comments
Hardness, Shore D	62	62	ISO 868
Film Tensile Strength at Yield, MD	50.0 MPa	7250 psi	ISO 527
Film Tensile Strength at Yield, TD	45.0 MPa	6530 psi	ISO 527
Film Elongation at Break, MD	400 %	400 %	ISO 527
Film Elongation at Break, TD	450 %	450 %	ISO 527
Elmendorf Tear Strength MD	25 g	25 g	ISO 6383-2
Elmendorf Tear Strength TD	45 g	45 g	ISO 6383-2
Elmendorf Tear Strength, MD	1.25 g/micron	31.8 g/mil	ISO 6383-2
Elmendorf Tear Strength, TD	2.25 g/micron	57.1 g/mil	ISO 6383-2
Dart Drop	12.0 g/micron	305 g/mil	F50; ASTM D1709
Dart Drop Test	240 g	0.529 lb	F50; ASTM D1709

Thermal Properties	Metric	English	Comments
Vicat Softening Point	75.0 °C	167 °F	ISO 306
Brittleness Temperature	<= -80.0 °C	<= -112 °F	ASTM D746

Processing Properties	Metric	English	Comments
Melt Temperature	200 - 225 °C	392 - 437 °F
Blow-up Ratio (BUR)	3.0 - 5.0	3.0 - 5.0