- RheTech Products FRP102-00 Polypropylene, Flame Retardant, Natural
RheTech Products FRP102-00 Polypropylene, Flame Retardant, Natural
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Flame Retardant |
| Manufacturer | RheTech Products |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | RheTech Products FRP102-00 Polypropylene, Flame Retardant, Natural.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Electrical component housingsInjection molding conditions reported in table.Information provided by RheTech Products.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.950 g/cc | 0.950 g/cc | 23/23°C; ASTM D792 |
| Linear Mold Shrinkage | 0.016 cm/cm | 0.016 in/in | ASTM D955 |
| Melt Flow | 10 g/10 min @Load 2.16 kg, Temperature 230 °C |
10 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 75 | 75 | ASTM D2240 |
| Tensile Strength at Break | 34.5 MPa | 5000 psi | 2 in/min; ASTM D638 |
| Flexural Modulus | 1.55 GPa | 225 ksi | Tangent; ASTM D790 |
| Izod Impact, Notched | 0.267 J/cm @Temperature 23.0 °C |
0.500 ft-lb/in @Temperature 73.4 °F |
ASTM D256 |
| Gardner Impact | 0.904 J | 0.667 ft-lb | ASTM D5420 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 98.9 °C | 210 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 54.4 °C | 130 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 191 - 199 °C | 375 - 390 °F | |
| Middle Barrel Temperature | 199 - 210 °C | 390 - 410 °F | |
| Front Barrel Temperature | 199 - 210 °C | 390 - 410 °F | |
| Nozzle Temperature | 204 °C | 400 °F | |
| Mold Temperature | 23.9 - 35.0 °C | 75.0 - 95.0 °F | |
| Drying Temperature | 51.7 - 65.6 °C | 125 - 150 °F | |
| Dry Time | 1 - 2 hour | 1 - 2 hour | |
| Moisture Content | <= 0.050 % | <= 0.050 % | Recommended |
| Injection Pressure | 2.76 - 8.27 MPa | 400 - 1200 psi | |
| Hold Pressure | 2.07 - 6.89 MPa | 300 - 1000 psi | |
| Back Pressure | 0.345 - 0.689 MPa | 50.0 - 100 psi |
Users viewing this material also viewed the following:
- Nyco RRIMGLOS® II Wollastonite
- Plastcom SLOVALEN PH 78 T 40 PP, 40% mineral filling
- Lucite International Diakon® Frost 952 51 Acrylic Polymer
- SABIC Innovative Plastics Ultem ATX153R PEI+PCE (Asia Pacific)
- Zhejiang Juner 302-G30 30% Glass Fibre Reinforced, Flammable Resistant, and Low Separate Out Mode
- A. Schulman POLYBATCH™ White 8000 AP Concentrate Based In LDPE
- CMW® ELKONITE® 50W3 Tungsten Copper material ASTM B702
- Alliance Polymers Viprene™ G65A-32U-NAT Thermoplastic Vulcanizate Elastomer
- BASF Ultramid® A3W BK 00464 PA66 (Conditioned)
- Elastocon TPE Technologies Elastocon® OF65 Thermoplastic Elastomer
Copyright © lookpolymers.com All Rights Reserved