Resinoid 2205 Phenolic Molding, Cellulose Reinforced
| Category | Polymer , Thermoset , Filled/Reinforced Thermoset , Phenolic , Phenolic, Novolac, Cellulose Filled |
| Manufacturer | Resinoid |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Resinoid 2205 Phenolic Molding, Cellulose Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by the manufacturer.The Resinoid 2000 organic fiber reinforced series compounds feature mechanical strength, dimensional stability, and shock resistance
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.40 g/cc | 0.0506 lb/in³ | ASTM D792A |
| Water Absorption | 0.28 % | 0.28 % | 24 hours R.T. ASTM D570 |
| Linear Mold Shrinkage | 0.0040 cm/cm | 0.0040 in/in | Positive Mold; ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 52.0 MPa | 7540 psi | ASTM D651 |
| Flexural Strength | 86.0 MPa | 12500 psi | ASTM D790 |
| Flexural Modulus | 4.80 GPa | 696 ksi | ASTM D790 |
| Compressive Strength | 207 MPa | 30000 psi | ASTM D695 |
| Izod Impact, Notched | 0.315 J/cm | 0.590 ft-lb/in | ASTM D256A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 238 °C | 460 °F | ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Strength | 14.6 kV/mm | 371 kV/in | Short Time; Dry; ASTM D149 |
| Arc Resistance | 120 sec | 120 sec | ASTM D495 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Mold Temperature | 155 - 180 °C | 311 - 356 °F |
Users viewing this material also viewed the following:
- Polymax® Maxelast® P1755 TPE, PP Overmold or Standalone use
- Polykemi AB POLYabs F00 GF15 ABS, Glass Fiber-Reinforced
- IRPC Polimaxx Polene 1100NN Polypropylene Homopolymer
- Solvay Specialty Polymers Meforex® 124 Ozone-Friendly CFC Replacement
- Shinil Chemical SHINFLAME PA-6 GF Flame Retardant Polymer Parts
- Tipco Tipcolene® TPE 1000 - Impact Modified Polypropylene Copolymer Compound with High Stiffness
- ELASTO UK Dryflex® 602300S SEBS Based Material, Filled Qualities, 30A Hardness, Black
- Arkema Group Kynar® FLEX 2800 PVDF (discontinued **)
Copyright © lookpolymers.com All Rights Reserved