Resinoid 2002-2 Phenolic Molding, Fabric Reinforced

Category Polymer , Thermoset , Filled/Reinforced Thermoset , Phenolic , Phenolic, Novolac, Fabric Filled
Manufacturer Resinoid
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Resinoid 2002-2 Phenolic Molding, Fabric Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Data provided by the manufacturer.The Resinoid 2000 organic fiber reinforced series compounds feature mechanical strength, dimensional stability, and shock resistance
Physical Properties Metric English Comments
Density 1.41 g/cc
0.0509 lb/in³
ASTM D792A
Water Absorption 0.30 %
0.30 %
24 hours R.T. ASTM D570
Linear Mold Shrinkage 0.0030 cm/cm
0.0030 in/in
Positive Mold; ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 55.0 MPa
7980 psi
ASTM D651
Flexural Strength 102 MPa
14800 psi
ASTM D790
Flexural Modulus 11.0 GPa
1600 ksi
ASTM D790
Compressive Strength 138 MPa
20000 psi
ASTM D695
Izod Impact, Notched 0.683 J/cm
1.28 ft-lb/in
ASTM D256A
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 260 °C
500 °F
ASTM D648
Processing Properties Metric English Comments
Mold Temperature 150 - 170 °C
302 - 338 °F