Resinlab® EP1320LV Heat Cure Epoxy Conformal Coating

Category	Polymer , Adhesive , Thermoset , Epoxy , Epoxy Adhesive
Manufacturer	Resinlab®
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Resinlab® EP1320LV Heat Cure Epoxy Conformal Coating.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Resinlab™ EP1320 and EP1320LV are one part heat cure epoxy conformal coatings. They can also be used as a small mass potting compounds, structural adhesives, or insulating polymer systems where the application requires low shrinkage and excellent adhesion to a wide variety of plastics, metals and circuit board materials. These products give very good environmental protection and dielectric properties over a wide temperature range. The primary difference between the two versions is the LV version has a lower high shear viscosity (higher press flow rate) to provide easier dispensing. The amount of sag upon curing is the same.Information Provided by Resinlab L.L.C., an Ellsworth Adhesives Company.

Physical Properties	Metric	English	Comments
Specific Gravity	1.30 g/cc	1.30 g/cc	TM R050-16
Water Absorption	0.13 % @Time 86400 sec	0.13 % @Time 24.0 hour	TM R050-35
Viscosity	40000 cP	40000 cP	RVT, #5, 2.5 rpm; TM R050-12

Mechanical Properties	Metric	English	Comments
Hardness, Shore D	85	85	TM R050-17
Tensile Strength at Break	10.3 MPa	1500 psi	TM R050-36
Tensile Strength, Ultimate	10.3 MPa	1500 psi	TM R050-36
Tensile Strength, Yield	2.76 MPa	400 psi	TM R050-36
Elongation at Break	10 - 15 %	10 - 15 %	TM R050-36
Tensile Modulus	0.345 - 0.483 GPa	50.0 - 70.0 ksi	TM R050-36
Compressive Yield Strength	89.6 MPa	13000 psi	TM R050-38
Compressive Strength	110 MPa	16000 psi	Break; TM R050-38
	124 MPa	18000 psi	Ultimate; TM R050-38
Compressive Modulus	4.14 GPa	600 ksi	TM R050-38
Adhesive Bond Strength	15.9 MPa	2300 psi	Lap shear; 2024 T3 Al Abraded / MEK Wipe; TM R050-37

Thermal Properties	Metric	English	Comments
CTE, linear	48.0 µm/m-°C	26.7 µin/in-°F
Thermal Conductivity	0.360 W/m-K	2.50 BTU-in/hr-ft²-°F
Maximum Service Temperature, Air	150 °C	302 °F
Minimum Service Temperature, Air	-40.0 °C	-40.0 °F
Glass Transition Temp, Tg	98.0 °C	208 °F	TM R050-25

Electrical Properties	Metric	English
Volume Resistivity	8.00e+14 ohm-cm	8.00e+14 ohm-cm
Dielectric Constant	3.5 @Frequency 100 Hz, Temperature 25.0 °C	3.5 @Frequency 100 Hz, Temperature 77.0 °F
Dielectric Strength	17.3 kV/mm	440 kV/in

Processing Properties	Metric	English
Cure Time	5.00 - 10.0 min @Temperature 150 °C	0.0833 - 0.167 hour @Temperature 302 °F
	15.0 min @Temperature 120 °C	0.250 hour @Temperature 248 °F
	30.0 min @Temperature 110 °C	0.500 hour @Temperature 230 °F

Descriptive Properties	Value	Comments
Color	Black