Tisan TISLAMID® 66 25% Glass Fiber Reinforced Flame Retardant (V0). Heat Stabilized Nylon 66

Category	Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Glass Fiber Filled, Flame Retardant
Manufacturer	Tisan Engineering Plastics
Trade Name	TISLAMID®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Tisan TISLAMID® 66 25% Glass Fiber Reinforced Flame Retardant (V0). Heat Stabilized Nylon 66.pdf
Price	EMAIL US sales@lookpolymers.com

Material Notes:

TISLAMID has a wide area of application in electric/electronic, automotive, durable goods and telecommunications industries. It demonstrates characteristics such as Excellent chemical resistanceElectric isolationEasy processabilityHigh mechanical resistanceExcellent flame retardanceHigh moisture absorptionExcellent temperature resistanceHigh performance / affordable priceAbrasion resistanceTISLAMID has an excellent resistance to weak alkalis and organic solvents. It has a good resistance to weak acids, alcohols, hydrocarbons, and engine fuels. It has a medium resistance to strong alkalis and a weak resistance to strong acids.

Physical Properties	Metric	English	Comments
Density	1.55 g/cc	0.0560 lb/in³	ISO 1183
Linear Mold Shrinkage	0.0030 cm/cm	0.0030 in/in
Ash	25 %	25 %	ISO 3451

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	140 MPa	20300 psi	ISO 527-2
Tensile Strength, Yield	140 MPa	20300 psi	ISO 527-2
Elongation at Break	3.0 %	3.0 %	ISO 527-2
Elongation at Yield	2.9 %	2.9 %	ISO 527-2
Modulus of Elasticity	8.50 GPa	1230 ksi	ISO 527-2
Izod Impact, Notched (ISO)	7.00 kJ/m²	3.33 ft-lb/in²	ISO 180

Thermal Properties	Metric	English	Comments
Melting Point	255 - 260 °C	491 - 500 °F
Vicat Softening Point	255 °C	491 °F	ISO 306
Heat Distortion Temperature	250 °C	482 °F	ISO 75-2
Flammability, UL94	V-0	V-0
Glow Wire Test	960 °C	1760 °F	60695-2-10

Electrical Properties	Metric	English	Comments
Comparative Tracking Index	300 V	300 V	TS EN 60112

Processing Properties	Metric	English	Comments
Feed Temperature	70.0 - 90.0 °C	158 - 194 °F
Rear Barrel Temperature	260 - 280 °C	500 - 536 °F	Aft-1. Region Temperature
Middle Barrel Temperature	260 - 280 °C	500 - 536 °F	Mid-2. Region Temperature
Front Barrel Temperature	260 - 280 °C	500 - 536 °F	Pre-3. Region Temperature
Nozzle Temperature	250 - 270 °C	482 - 518 °F
Melt Temperature	260 - 290 °C	500 - 554 °F
Drying Temperature	90.0 - 100 °C	194 - 212 °F	Predrying Temperature
Dry Time	3 - 4 hour	3 - 4 hour	Predrying Time
Moisture Content	1.8 %	1.8 %	ISO 62

Descriptive Properties	Value	Comments
Block Temperature	75-85°C

Users viewing this material also viewed the following: