Bulk Molding Compounds BMC HT12-1026 Unsaturated Polyester Bulk Molding Compound

Category	Polymer , Thermoset , Polyester, TS , Polyester (Thermoset) - Rigid
Manufacturer	BMC - Bulk Molding Compounds Inc.
Trade Name	BMC
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Bulk Molding Compounds BMC HT12-1026 Unsaturated Polyester Bulk Molding Compound.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

BMC HT12-1026 is a highly engineered Unsaturated Polyester Bulk Molding Compound developed for automotive under-hood applications. This compound is specified by Ford motor company for solenoid caps. Due to its excellent heat resistance and dimensional stability it performs well in automotive applications.Information provided by Bulk Molding Compounds, Inc.

Physical Properties	Metric	English	Comments
Density	1.75 - 1.95 g/cc	0.0632 - 0.0704 lb/in³	Molded
Linear Mold Shrinkage	0.0015 - 0.0025 cm/cm	0.0015 - 0.0025 in/in

Mechanical Properties	Metric	English
Hardness, Barcol	30 - 35	30 - 35
Tensile Strength	67.6 - 81.4 MPa	9800 - 11800 psi
Flexural Strength	134 - 162 MPa	19500 - 23500 psi
Flexural Modulus	12.4 - 13.8 GPa	1800 - 2000 ksi
Compressive Strength	149 - 177 MPa	21600 - 25600 psi
Izod Impact, Notched	2.72 - 3.79 J/cm	5.10 - 7.10 ft-lb/in

Thermal Properties	Metric	English	Comments
Deflection Temperature at 1.8 MPa (264 psi)	218 - 260 °C	425 - 500 °F
Flammability, UL94	HB	HB	This product is not currently UL listed.

Electrical Properties	Metric	English	Comments
Dielectric Strength	13.7 - 15.6 kV/mm	347 - 397 kV/in	short time
Arc Resistance	180 sec	180 sec

Processing Properties	Metric	English	Comments
Processing Temperature	143 - 171 °C	290 - 340 °F