Ravago Manufacturing Americas Hylon® N1040ML Nylon 6/6 (Cond)
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | Ravago Manufacturing Americas, LLC |
| Trade Name | Hylon® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Ravago Manufacturing Americas Hylon® N1040ML Nylon 6/6 (Cond).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Ravago.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.49 g/cc | 0.0538 lb/in³ | DAM; ASTM D792 |
| Water Absorption | 0.60 % | 0.60 % | 24 hrs, DAM; ASTM D570 |
| Linear Mold Shrinkage | 0.0070 - 0.010 cm/cm | 0.0070 - 0.010 in/in | 0.125 in, DAM; ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 62.1 MPa | 9000 psi | ASTM D638 |
| Elongation at Break | 6.0 % | 6.0 % | ASTM D638 |
| Flexural Strength | 82.7 MPa | 12000 psi | ASTM D790 |
| Flexural Modulus | 2.76 GPa | 400 ksi | ASTM D790 |
| Izod Impact, Notched | 0.641 J/cm | 1.20 ft-lb/in | 73°F; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 204 °C | 400 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 149 °C | 300 °F | Unannealed; ASTM D648 |
| Flammability, UL94 | HB | HB | 0.0591 in, BK |
| HB | HB | 0.0591 in, NC | |
| HB | HB | 0.118 in, BK | |
| HB | HB | 0.118 in, NC |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 6.0 @Frequency 100 Hz |
6.0 @Frequency 100 Hz |
ASTM D150 |
| Dielectric Strength | 20.9 kV/mm | 530 kV/in | ASTM D149 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 282 - 299 °C | 540 - 570 °F | |
| Mold Temperature | 65.6 - 98.9 °C | 150 - 210 °F | |
| Drying Temperature | 73.9 °C | 165 °F | |
| Dry Time | 2 - 4 hour | 2 - 4 hour | |
| Moisture Content | 0.20 % | 0.20 % | |
| Back Pressure | 0.138 - 0.414 MPa | 20.0 - 60.0 psi | |
| Screw Speed | 40 - 120 rpm | 40 - 120 rpm |
Users viewing this material also viewed the following:
- Nabaltec GRANALOX® NM 9620 Ceramic Bodies
- Pacific Sintered Materials BZ-111-UC Yellow Brass Powdered Metal
- Kuraray HYBRAR® PS3 Thermoplastic Rubber-Polystyrene Blend
- Tra-Con Tra-Bond 2159 Heat Conductive Electrically Insulating Compound
- Dow Corning Z-6018 INTERMEDIATE
- DuPont Teijin Films Teonex® Q51 Polyester Film, 48 Gauge
- BASF Elastollan® 1175AW Polyether Type Polyurethane Elastomer
- 3M Panagraphics™ III Wide Width Flexible Substrate
- 3M 7962MP High Performance Adhesive Transfer Tapes with Adhesive 200MP
- Beijing Evergrow Resources Glass Filled Nylon
Copyright © lookpolymers.com All Rights Reserved