- Ravago Manufacturing Americas Hylon® N1033STHL Nylon 6/6 (Cond)
Ravago Manufacturing Americas Hylon® N1033STHL Nylon 6/6 (Cond)
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Heat Stabilized |
| Manufacturer | Ravago Manufacturing Americas, LLC |
| Trade Name | Hylon® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Ravago Manufacturing Americas Hylon® N1033STHL Nylon 6/6 (Cond).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Ravago.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.33 g/cc | 0.0480 lb/in³ | DAM; ASTM D792 |
| Water Absorption | 0.40 % | 0.40 % | 24 hrs, DAM; ASTM D570 |
| Linear Mold Shrinkage | 0.0030 - 0.0050 cm/cm | 0.0030 - 0.0050 in/in | 0.125 in, DAM; ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 60 | 60 | ASTM D785 |
| Tensile Strength at Break | 100 MPa | 14500 psi | ASTM D638 |
| Elongation at Break | 5.0 % | 5.0 % | ASTM D638 |
| Flexural Strength | 145 MPa | 21000 psi | ASTM D790 |
| Flexural Modulus | 5.52 GPa | 800 ksi | ASTM D790 |
| Izod Impact, Notched | 2.14 J/cm | 4.00 ft-lb/in | 73°F; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Flammability, UL94 | HB | HB | 0.0591 in, BK |
| HB | HB | 0.118 in, BK |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 282 - 299 °C | 540 - 570 °F | |
| Mold Temperature | 65.6 - 98.9 °C | 150 - 210 °F | |
| Drying Temperature | 73.9 °C | 165 °F | |
| Dry Time | 2 - 4 hour | 2 - 4 hour | |
| Moisture Content | 0.18 % | 0.18 % | |
| Back Pressure | 0.138 - 0.414 MPa | 20.0 - 60.0 psi | |
| Screw Speed | 40 - 120 rpm | 40 - 120 rpm |
Users viewing this material also viewed the following:
- Nye Lubricants 363F-WHITE (RL) Synthetic Oil
- Plastcom SLOVALEN PQ 83 N PP, imp. strength
- Termopol Termoton® K6GA4040A TPE Compound, based on SEBS and Polyolefins
- TSE Industries Millathane® 5004 Millable Polyurethane Elastomer, 350ºF Cure Temperature
- Lehmann & Voss LUVOCOM® 1105/XCF/25 PEEK, with carbon fiber
- Sinotek Materials HFB Board Heat Insulation Material Ceramic Fiber Board, White
- Solvay Sulfuric Acid 78% Technical Grade
- Wieland 1910 Wilaform Gold
- Chi Mei Polylac® PA-764B ABS - Flame Retardant
Copyright © lookpolymers.com All Rights Reserved