- Ravago Manufacturing Americas Hylon® N1013STL Nylon 6/6 (Cond) (discontinued **)
Ravago Manufacturing Americas Hylon® N1013STL Nylon 6/6 (Cond) (discontinued **)
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Impact Grade |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Ravago Manufacturing Americas Hylon® N1013STL Nylon 6/6 (Cond)
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Ravago.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.18 g/cc | 0.0426 lb/in³ | DAM; ASTM D792 |
| Water Absorption | 0.70 % | 0.70 % | 24 hrs, DAM; ASTM D570 |
| Linear Mold Shrinkage | 0.0050 - 0.0080 cm/cm | 0.0050 - 0.0080 in/in | 0.125 in, DAM; ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 55.2 MPa | 8000 psi | ASTM D638 |
| Elongation at Break | 8.0 % | 8.0 % | ASTM D638 |
| Flexural Strength | 48.3 MPa | 7000 psi | ASTM D790 |
| Flexural Modulus | 2.41 GPa | 350 ksi | ASTM D790 |
| Izod Impact, Notched | 2.14 J/cm | 4.00 ft-lb/in | 73°F; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Flammability, UL94 | HB | HB | 0.0591 in, BK |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 282 - 299 °C | 540 - 570 °F | |
| Mold Temperature | 65.6 - 98.9 °C | 150 - 210 °F | |
| Drying Temperature | 73.9 °C | 165 °F | |
| Dry Time | 2 - 4 hour | 2 - 4 hour | |
| Moisture Content | 0.18 % | 0.18 % | |
| Back Pressure | 0.138 - 0.414 MPa | 20.0 - 60.0 psi | |
| Screw Speed | 40 - 120 rpm | 40 - 120 rpm |
Users viewing this material also viewed the following:
- Fine Organics FINALUX G 712 Lubricant Additive
- Ferro EG 2992 Glaze and Sealant Glass
- LG Chemical SG175NS ABS, Super Surface Gloss, General Anti-Static
- A. Schulman SCHULAMID® 66 MV3HI High Impact Nylon 6/6
- A. Schulman POLYBATCH™ White 8153/UV2 Concentrate Based In Polyethylene
- Polyplastics Duranex® 209A Polybutylene Terephthalate (PBT), Low friction, Low wear
- ExxonMobil SAE 40 Mobilgard M30 Series
- Arlon LW202Bxx-P1 0.020" (0.508 mm) Self-Fusing Silicone Tape (Triangular, Unsupported) with Poly Interleave
- Bhansali Engineering Abstron HI-40 B ABS High Impact Injection Molding
Copyright © lookpolymers.com All Rights Reserved