- Acrylonitrile Butadiene Styrene (ABS), Molded
- Ravago Manufacturing Americas Hylac® EX28 ABS
Ravago Manufacturing Americas Hylac® EX28 ABS
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Molded |
| Manufacturer | Ravago Manufacturing Americas, LLC |
| Trade Name | Hylac® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Ravago Manufacturing Americas Hylac® EX28 ABS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Entec's proprietary products include a full range of compounds in the Nylon 6/6, Nylon 6, ABS, PBT, Polycarbonate, PC/ABS, PC/ASA, PC/PBT, and PPO/PPE resin families.Information provided by Ravago.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.04 g/cc | 0.0376 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0030 - 0.0070 cm/cm | 0.0030 - 0.0070 in/in | ASTM D955 |
| Melt Flow | 1.75 g/10 min @Load 3.80 kg, Temperature 230 °C |
1.75 g/10 min @Load 8.38 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 101 | 101 | ASTM D785 |
| Tensile Strength, Yield | 44.1 MPa | 6400 psi | ASTM D638 |
| Elongation at Break | 40 % | 40 % | ASTM D638 |
| Tensile Modulus | 2.43 GPa | 352 ksi | ASTM D638 |
| Flexural Yield Strength | 62.1 MPa | 9000 psi | ASTM D790 |
| Flexural Modulus | 2.24 GPa | 325 ksi | ASTM D790 |
| Izod Impact, Notched | 3.52 J/cm | 6.60 ft-lb/in | 0.25 in; ASTM D256 |
| 4.06 J/cm | 7.60 ft-lb/in | 73°F, 0.125 in; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 115 µm/m-°C @Temperature -40.0 - 176 °C |
64.0 µin/in-°F @Temperature -40.0 - 349 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 97.2 °C | 207 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 87.2 °C | 189 °F | Unannealed; ASTM D648 |
| Vicat Softening Point | 102 °C | 215 °F | ASTM D1525 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | ASTM D257 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Zone 1 | 191 - 210 °C | 375 - 410 °F | |
| Zone 2 | 191 - 210 °C | 375 - 410 °F | |
| Zone 3 | 199 - 221 °C | 390 - 430 °F | |
| Zone 4 | 199 - 221 °C | 390 - 430 °F | |
| Zone 5 | 199 - 221 °C | 390 - 430 °F | |
| Adapter Temperature | 221 - 241 °C | 430 - 465 °F | |
| Die Temperature | 221 - 241 °C | 430 - 465 °F | |
| Drying Temperature | 85.0 °C | 185 °F | |
| Dry Time | 3 hour | 3 hour | |
| Moisture Content | <= 0.020 % | <= 0.020 % |
Users viewing this material also viewed the following:
- Ineos H12Z-02 Polypropylene Homopolymer, Antistatic and Nucleated
- Karina E 854-35/1-Y-ERYB Ivory PVC Compound
- LG Chemical LUPOL GP-3154F General Purpose Polypropylene, 15% Mineral Fillers, High Modulus, Flame Retardant
- Saint-Gobain Norton® V760 High Density Vibration
- Dow Corning SYL-OFF® PMCPSL 560 Coating
- CMW® ELKONITE® 3150 Silver Tungsten Carbide contact material ASTM B663 Table 2, Class B
- Eurostar Starflam PF0057E PA6, 25% Glass Filled, Injection Molded
- Azoty Tarnow™ Tarnamid® T-29 MCS Polyamide 6 - Colored
- Taiwan Sheen Soon Sheenthane® A9830 Thermoplastic Polyurethane Elastomer
- Ametek P316L P/M Stainless Steel, Sintered from 6.83 g/cc Green Density
Copyright © lookpolymers.com All Rights Reserved