- A. Schulman SCHULAMID® 66 GF50 50% Glass Fiber Reinforced 66
A. Schulman SCHULAMID® 66 GF50 50% Glass Fiber Reinforced 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 50% Glass Fiber Filled |
| Manufacturer | A. Schulman, Inc. |
| Trade Name | SCHULAMID® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | A. Schulman SCHULAMID® 66 GF50 50% Glass Fiber Reinforced 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by A. Schulman.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.57 g/cc | 1.57 g/cc | ISO 1183/1 |
| Linear Mold Shrinkage | 0.0030 - 0.010 cm/cm @Thickness 3.175 mm |
0.0030 - 0.010 in/in @Thickness 0.1250 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 230 MPa | 33400 psi | ISO 527 |
| Tensile Modulus | 16.0 GPa | 2320 ksi | ISO 527 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 250 °C | 482 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 250 °C | 482 °F | ISO 75 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 143 - 154 °C | 290 - 310 °F | |
| Mold Temperature | 65.6 - 93.3 °C | 150 - 200 °F | |
| Drying Temperature | 79.4 °C | 175 °F | |
| Dry Time | 2 - 4 hour | 2 - 4 hour | Predrying |
Users viewing this material also viewed the following:
- Premix Premi-Glas® 2205-30 CR-SX Fiberglass Reinforced SMC
- Polykemi AB POLYabs F00 ABS
- Kolon KOLEFIN® KO133GM40 M/F Reinforced Polypropylene
- Chengdu Polyster KP-200H Silicone Masterbatch
- Entec Hylox® 9030 PBT, 30% Glass Reinforced
- Donnelly Bros APG #2 Super Clean All Purpose Mold Grease
- ConocoPhillips Hydroclear® 100 Gas Compressor Fluid
- Abatron AboCast 8503-10/AboCure 8503-10 5-Minute Epoxy
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 20 PHR N774 Filler
- A. Schulman POLYBLAK™ 3123 Premium Black Color Concentrate, 50% Carbon Black Based In LDPE
Copyright © lookpolymers.com All Rights Reserved