Ravago Manufacturing Americas Hybrid S451H Acrylonitrile Butadiene Styrene + PC Alloy
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC) |
| Manufacturer | Ravago Manufacturing Americas, LLC |
| Trade Name | Hybrid |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Ravago Manufacturing Americas Hybrid S451H Acrylonitrile Butadiene Styrene + PC Alloy.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Available in North America Flame Retardant High Flow RoHS Compliant UL File Number: E157012 Form: Pellets Processing Method: Injection Molding Information provided by Ravago
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.21 g/cc | 1.21 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | ASTM D955 |
| Melt Flow | 18 g/10 min @Load 2.16 kg, Temperature 260 °C |
18 g/10 min @Load 4.76 lb, Temperature 500 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 63.4 MPa | 9200 psi | ASTM D638 |
| Elongation at Break | 30 % | 30 % | ASTM D638 |
| Flexural Strength | 82.7 MPa | 12000 psi | ASTM D790 |
| Flexural Modulus | 2.41 GPa | 350 ksi | ASTM D790 |
| Izod Impact, Notched | 5.87 J/cm @Thickness 3.17 mm |
11.0 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 92.8 °C | 199 °F | Unannealed; ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 249 - 260 °C | 480 - 500 °F | |
| Middle Barrel Temperature | 254 - 266 °C | 490 - 510 °F | |
| Front Barrel Temperature | 260 - 271 °C | 500 - 520 °F | |
| Nozzle Temperature | 260 - 277 °C | 500 - 530 °F | |
| Mold Temperature | 71.1 - 93.3 °C | 160 - 200 °F | |
| Drying Temperature | 104 - 110 °C @Time 7200 - 14400 sec |
220 - 230 °F @Time 2.00 - 4.00 hour |
|
| Dry Time | <= 10.0 hour | <= 10.0 hour | |
| Moisture Content | <= 0.040 % | <= 0.040 % | Suggested Maximum |
| Injection Pressure | 5.52 - 11.7 MPa | 800 - 1700 psi | |
| Back Pressure | 0.345 - 0.827 MPa | 50.0 - 120 psi | |
| Shot Size | 40 - 80 % | 40 - 80 % | |
| Screw Speed | 40 - 60 rpm | 40 - 60 rpm |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Injection Rate | Moderate |
Users viewing this material also viewed the following:
- Ineos Nova PS 2520 Crystal Polystyrene (discontinued **)
- Karina E 06/815-FC-LMP MB Concentration de Pigment Blue for PVC
- Saint-Gobain Norton® V990 Poly Liner Pressure Sensitive Adhesive Foam Sealant
- SABIC Innovative Plastics LNP THERMOCOMP LF002 PEEK
- Tra-Con Tra-Bond 216R02 Quick Set Electrical Insulator
- Hexcel® Redux® 330M Epoxy film adhesives for the bonding and finishing of composites
- American Polymers API 390 Polystyrene
- Total PPC 3650 Polypropylene, Heterophasic Copolymer, Injection Molding
- Beijing Ranger Chem PBT-201-G15 202 Environmental Protection Flame Retarding FR PBT
Copyright © lookpolymers.com All Rights Reserved